引起反白口的主要原因是残余镁量，特别是残余稀土量过高，防止措施是采用稀土含量较低的球化剂，提高球化处理温度和浇注温度。
Too high residual magnesium content, and especially too high residual rare earth content is the main reason causing reverse chill defect. So them…
引起反白口的主要原因是残余镁量，特别是残余稀土量过高，防止措施是采用稀土含量较低的球化剂，提高球化处理温度和浇注温度。
Too high residual magnesium content, and especially too high residual rare earth content is the main reason causing reverse chill defect. So them…