给出了焊接残余应力与局部焊后热处理应力的试验结果与模拟结果的对比。
Experiment results of welding residual stress and the stress after local post weld heat treatment are compared with numerical simulation.
模拟钢轨焊接及焊后热处理工况,采用热膨胀方法分别测定uic 900a及u75 V钢轨钢的连续冷转变曲线(CCT曲线)。
By simulating welding and simulating heat treatment after welding, CCT Curves of UIC900A and U75V rail steels are determined by the expansion method.
用焊接热模拟方法确定了焊后热处理工艺参数。
The technological parameter of post-welded heat-treatment is determined by welding thermal simulation test.
采用焊接热模拟的方法,模拟HAZ粗晶区组织,并在不同回火参数下对试样进行焊后热处理。
By use of the method of welding thermal simulation, the morphology in HAZ was simulated and the post-weld heat treatment under different tempering parameter to the test specimen was carried out.
采用焊接热模拟的方法,模拟HAZ粗晶区组织,并在不同回火参数下对试样进行焊后热处理。
By use of the method of welding thermal simulation, the morphology in HAZ was simulated and the post-weld heat treatment under different tempering parameter to the test specimen was carried out.