将6020扩展到模压淬火产品的尝试遇到了几个问题。
Attempts to extend 6020 to a press quenched product were met with several problems.
本发明的主要目的是提供可模压淬火的基本不含铅的合金。
The primary object of the present invention is to provide a substantially lead free alloy that is press quenchable.
模压淬火6020合金的期望产品形式是杆材、棒材和线材应用。
The product forms for which a press quenched 6020 alloy is desired are rod, bar, and wire applications.
本发明的模压淬火6020合金含有硅、镁、铜、铁、锰、铬和锡。
The press quench 6020 alloy of the present invention contains silicon, magnesium, copper, iron, manganese, chromium, and tin.
本发明涉及一种模压淬火6xxx系列铝合金、优选铝合金6020的方法。
The invention relates to a method of press quenching a 6xxx series aluminum alloy, preferably aluminum alloy 6020.
对于这种性质的模压淬火产品，典型使用825 - 900 ？的坯料温度。
For press quench products of this nature, billet temperatures of 825 to 900. degree.
本发明的另一个目的是提供可用作含铅合金6262 -T6的直接替代物的模压淬火合金。
A further object of the invention is to provide a press quench alloy that can be used as a direct replacement for lead containing alloy 6262-t6.
在上面概述的方法之后将产生显示出良好强度和伸长率的细晶粒、完全再结晶、模压淬火的产品。
Following the method outlined above will produce a fine-grained, fully recrystallized, press quenched product that demonstrates good strength and elongation.
本发明的另一个目的是提供具有提高的挤压生产率和良好的机械性能和机械加工性能的模压淬火合金。
Another object of the present invention is to provide a press quench alloy with enhanced extrusion productivity and good mechanical properties and machinability.
这种经过模压淬火的铝合金可以被用作含铅合金6262-T6的直接替代物，从而解决了可能引起的任何环境问题。
This press-quenched aluminum alloy can be used as a direct replacement for lead containing alloy 6262-T6, thereby addressing any environmental issues that may be raised.
这种经过模压淬火的铝合金可以被用作含铅合金6262-T6的直接替代物，从而解决了可能引起的任何环境问题。
This press-quenched aluminum alloy can be used as a direct replacement for lead containing alloy 6262-T6, thereby addressing any environmental issues that may be raised.