所以，在钢锭模内析出的气体没有沸腾钢多，但又在钢锭头产形成足够的气泡抵消大部分钢的收缩。
So less gas is. given off in the mould than with rimming steel, but enough bubbles form at the top of the ingot to counteract most of the shrinkage.
指出，拉丝模内孔之所以产生裂纹，是由于压模收缩比太小的原因。
It is indicated the said crack is due to too small shrinkage ratio of the compacting die.
并用压坯单重递减法试验证实，当将压模收缩比增加到1 2 2以上时，可以保证压坯内孔不出现裂纹。
The test of single compact weight decrease proved that when the shrinkage ratio of the compacting die is increased to over 1.22, there is no more crack initiated in the compact inner hole.
并用压坯单重递减法试验证实，当将压模收缩比增加到1 2 2以上时，可以保证压坯内孔不出现裂纹。
The test of single compact weight decrease proved that when the shrinkage ratio of the compacting die is increased to over 1.22, there is no more crack initiated in the compact inner hole.