抽取的检验样品应当迅速放入密闭容器中(塑料袋、铁罐或磨口玻璃瓶)。
The inspection samples shall be put in airtight containers (plastic bags, cans or ground glass bottles) as soon as they are fetched.
循环寿命测试，球磨的样品经过50次循环其容量衰减到40%，非球磨样品经25次的循环即衰减到同样程度。
Cycling life tests investigated that the capacity of alloy prepared by ball milling decreased to 40% after 50 cycles, while the solid-state diffusion method just 25 cycles.
实验还表明，球磨弥散剂对样品的性能也有较大影响。
It also shows that the dispersing medium can influence its properties greatly.
结果发现，球磨可形成合金化，随球磨时间的增加，样品的非晶化逐渐加强。
The results show that an alloy may be formed by ball-milling and amorphous character is enhanced with the increasing of the milling time.
文章通过选样、筛分、磨样、烘样、溶样等手段对样品进行处理，并按标准ISO9507-1990对样品进行全铁含量检测，考察铁含量随不同粒径块铁矿的变化。
The samples were dealt with selection, sieve, grinding, drying and dissolving. The samples were tested according to ISO9507-1990, the variation of iron content at different particle sizes was studied.
文章通过选样、筛分、磨样、烘样、溶样等手段对样品进行处理，并按标准ISO9507-1990对样品进行全铁含量检测，考察铁含量随不同粒径块铁矿的变化。
The samples were dealt with selection, sieve, grinding, drying and dissolving. The samples were tested according to ISO9507-1990, the variation of iron content at different particle sizes was studied.