综述了木材的不同阻燃机理和目前主要应用的木材阻燃处理工艺，另外，还对白俄罗斯目前应用的木材阻燃处理技术进行了介绍。
In this paper, different kinds of mechanism and treatments of wood fire retardant applied at present were discussed. In addition, treatment applied in Belarus was introduced.
探讨了超声波应用于木材阻燃浸渍处理过程的可行性，同时讨论了超声波试验参数频率、声强、辐射时间等的选择。
This paper explores the feasibility of ultrasonic technology leading to produce fire-retardant wood and test conditions such as frequency, sound intensity and time etc.
通过本研究不仅可以对木材燃烧机理的深入研究，而且对于木材进行阻燃处理提供理论依据。
It can provide some theoretical bases for the further study on the mechanism of wood combustion and fire retarding treatment on wood.
研究结果表明：DPB是一种性能较好的木材阻燃剂、但处理木材的DPB易流失、且化学稳定性很低。
The experiments showed that DPB is a well wood fire retardant, but it's leachable and chemistry stability is low.
实验表明：DPB是一种性能较好的木材阻燃剂，但DPB处理木材的抗胀缩率和阻湿率值均很低。
The experiments showed that DPB is a well wood fire retardant. but ASE and MEE of modified wood are low.
结果表明，经过阻燃处理的木材其氧指数和剩碳率比未处理的木材升高，而热降解反应活化能和分解温度降低。
Experimental data showed that for the treated wood there was an increase in char yield and LOI, and decreases in activation energy and temperature of decomposition.
结果表明：火灾发生过程中未处理木材、阻燃浸渍处理和涂刷防火徐料木材内部温度上升过程出现5个阶段；
The results showed that : there were five stages in the rising process of the internal temperature of untreated, fire - retardant solution soaked, and fire - proof paint coated wood during the fire ;
结果表明：火灾发生过程中未处理木材、阻燃浸渍处理和涂刷防火徐料木材内部温度上升过程出现5个阶段；
The results showed that : there were five stages in the rising process of the internal temperature of untreated, fire - retardant solution soaked, and fire - proof paint coated wood during the fire ;