指出偏析不是引起硅脆的根本原因，硅脆是固溶体发生有序转变的结果。
The segregation was found not to be a main cause of the Si brittleness, which may arises from ordered transformation of the solid solution.
结果发现，其固溶态含有大量有序畴的不均匀固溶体；
The results show that there are lots of uneven ordering domain after solution treatment.
结果发现，其固溶态含有大量有序畴的不均匀固溶体；
The results show that there are lots of uneven ordering domain after solution treatment.