在最终热处理后翼缘法兰的垫片的端面应进行加工。
The gasket faces of girth flanges shall be machined after final heat treatment.
齿轮的最终热处理采用使零件变形较小的齿面高频淬火；
Gear final heat treatment using the parts deformation small tooth surface quenching;
介绍了高强度管坯的生产流程及锻后热处理、最终热处理工艺。
The production flow, after forged heat treatment and final heat treatment process for the high strength tube blank have been described in this article.
在最终热处理采用循环淬火晶粒细化效果好，三次淬火细化的晶粒可达到10级。
In the final heat treatment using circular quenching grain refinement effect is good, three times quenching refinement of grain can achieve 10 levels.
对发电机轴端头的最终热处理工艺进行了研究和改进，筛选出了最佳工艺条件并进行了实施。
This article has described the research and upgrading of the final heat treatment process for the generator shaft end, the optimized process has been selected and put into the operation.
对4343/ 30 0 3铝合金复合硬钎焊板最终热处理工艺进行了研究，运用方差分析方法对影响因素进行了分析。
Using square error analysis method, the finishing heat treatment process of 4343/3003 aluminum sandwich brazing sheet is studied.
运用正交试验法对奥贝球铁生产拖拉机最终传动从动齿轮的热处理工艺进行了优化试验。
The optimizing experiments on the heat treatment process for the final transmission driven gear made of austempered ductile iron (ADI) were carried out using orthogonal test.
研究结果表明，双金属材料确定后，热处理芯轴尺寸和再结晶退火温度决定双金属环的最终尺寸。
The research result indicates that, when bimetal material is certain, the size of heat treatment mandrill and the temperature of re-crystallized anneal would decide the end size of bimetals wreaths.
它能够实现从钢水到完整的最终产品的不间断生产，包括在线热处理和质量检查，可显著降低成本。
It enables uninterrupted production from liquid steel to the finished product, including on-line heat treatments and inspection procedures which leading to substantial cash-cost.
主要研究了用h 13制作LG80孔型的热处理工艺，经过反复的实验，最终确定了H 13的热处理工艺。
The heat treatment process for LG80 groove made with H13 is researched by repeated experiments, and finally determined.
结果表明，该轴热处理上存在的不合理之处，导致轴在服役早期出现微裂纹，部分微裂纹在工作应力的作用下疲劳扩展，最终产生疲劳断裂。
The results show that the axle has defects in heat treatment, which leads to micro crack in early stage of service life and the extended crack finally causes fatigue fracture.
其工艺要点是合理的热处理技术的解决。最终为用户提供合格的磁钢产品。
It was found that a proper heat treatment procedure was essential to making these steels, and hence to providing the users with the magnetic steels of high quality.
通过试验研究，最终完成了该钢种的成分方案、工艺方案及热处理方案的设计，对指导工业生产实践起到了积极的作用。
The plans of chemical composition, process and hot treatment which was finished by the experiment and research will play an active role in conducting the industry production.
根据强韧性匹配原则，最终确定了适宜的热处理工艺参数。
The proper heat treatment parameters are firmed according to the principle of matching for strength and toughness.
直接淬火，名词，在形变热处理过程中，最终热变形之后立即进行淬火。
Direct quenching, n-in thermomechanical processing, quenching immediately following the final hot deformation.
直接淬火，名词，在形变热处理过程中，最终热变形之后立即进行淬火。
Direct quenching, n-in thermomechanical processing, quenching immediately following the final hot deformation.