对应更高的衬底温度,因薄膜中的氢不能完全中止纳米晶粒界面的悬键,使薄膜能带带尾加宽。
Further increasing the substrate temperature broadens the band tail width of the films because the hydrogen content is too low to passivate the dangling bonds at the NC silicon grain surface.
实验结果表明:多晶硅薄膜的晶粒界面态和硅离子注入后多晶硅薄膜的晶粒组成结构是密切相关的。
The results show that the properties of grain-boundary states in recrystallized polysilicon films sharply depends on the crystallographic structure of the films.
研究了DD 8高温合金在平界面及胞晶区的晶粒竞争生长。
The competitive grain growth of DD8 high temperature alloy in planar and cellular interface region has been investigated.
当晶粒尺寸减少时,晶粒边界或界面的体积分数有很大的增加。
As the grain size decreases, there is a significant increase in the volume fraction of grain boundaries or interfaces.
新晶粒的界面迁移速率在迁移过程中不断下降,以至最后几乎停止迁移。
The migration rate of new grains continuously decreased, many of them even stopped growing at a certain size and remained unchanged during long annealing time.
复合材料界面结构由芯材扩散层、激冷凝固层、方向性生长层和胞状晶粒层组成。
The interface structure of composite consists of core material diffusion layer, chilling solidified layer, directional growth layer, and cellular granular layer.
晶粒长大、晶界面积减少以及镀层表面生成较厚的、致密的氧化膜是耐蚀性提高的主要原因。
The main cause of better corrosion resistance was due to growth of granules, decrease of grain boundary area, and formation of thick and compact oxidation film on the coating surface.
晶粒长大、晶界面积减少以及镀层表面生成较厚的、致密的氧化膜是耐蚀性提高的主要原因。
The main cause of better corrosion resistance was due to growth of granules, decrease of grain boundary area, and formation of thick and compact oxidation film on the coating surface.