本实验研制的超速凝超早强水泥中的微集料掺加量高达13%。
Amount of microaggregate added in this kind of cement was up to 13%.
本实验研制的超速凝超早强水泥中的微集料掺加量高达13%。
Super quick setting and super high early strength cement was studied. Amount of microaggregate added in this kind of cement was up to 13%.
将绝热量热计与微机联用,研究了木质素磺酸盐对COP快硬早强水泥水化速率的影响。
The results show that lignin sulfonate serves the good function as reqlllating the coagulation time of COP rapid hardening high strength cement.
近年来,早强型水泥引起的混凝土结构工程裂缝问题日渐突出。
Concrete structure crack problem caused by high-early-strength cement is outstanding recently.
以激发反应原理研制的超早强熟料,并用以激发粉煤灰的潜在活性制成粉煤灰硅铝酸盐水泥。
Super high early strength clinker has been developed and flyash aluminosilicate cement has been produced on the principle of excitation reaction.
根据微细水泥的特点,开发出了适合微细水泥-漂珠低密度水泥体系的复合早强剂和密度1。
According to the characteristics of micro-fine cement, a compound early strength agent and light weight cement with 1.
虽然贝利持矿物早期强度较低,但通过引入早强矿物或加适当的稳定活化剂或低温煅烧等方式可以解决贝利特水泥早强低的问题。
The problem of the low early strength of Belite cement can be solved by adding minerals which has high early strength or appropriate activation or burning at low temperature.
当赤泥配比达35%时,可生产高标号早强快硬水泥。
The addition of red mud up to 35% is still possible to produce high early strength cement.
该项技术不需传统生产水泥的方法—二磨一烧,就可生产合格的早强、高强水泥。
By use of this technology an early high-strength cement can be obtained without traditional steps "two-grinding and one burning".
硫铝酸盐水泥比硅酸盐水泥具有早强、高强、抗渗、耐侵蚀、抗冻、微膨胀等性能。
Sulphoaluminate cement has better properties than Portland cement, high strength, fast hardening, impermeability, corrosive resistance, frost resistance, expansive property and so on.
结果表明,碱-矿渣水泥具有早强、高强、低水化热和高耐久性等优良性能,但是干缩较大;
The results show that AS cement possesses high early strength, low hydration heat and durability, but its shrinkage rate is higher than that of portland cement.
且外部活化的应用,对水泥呈现出助磨、早强、减水等三种有益的功能。
Moreever, the application of outer activation is beneficial to grind-aiding, early strength and water-reducing etc.
早强组分可缩短水泥凝结时间,但掺量不宜太大;
The accelerator can shorten the setting time, the dosage yet can not be too much.
处理后铬渣加入适量硫酸钠,渗入水泥砂浆中可以起到早强减水作用。
The addition of the treated chromic refuse with proper amount of sodium sulfate into cement paste has shown an important role in q...
在CGM高强无收缩灌浆料的基础上,通过改变水泥品种和添加早强剂研制出CGM抢修料。
A new CGM fast-aid repair material was developed by changing the kind of cement and adding hardening accelerator based on the CGM High Strength Non-Shrinkage Grouting material.
处理后铬渣加入适量硫酸钠,渗入水泥砂浆中可以起到早强减水作用。
The addition of the treated chromic refuse with proper amount of sodium sulfate into cement paste has shown an important role in quicker water absorption and earlier hardening.
加入早强剂与增加胶乳中苯乙烯的含量可以增加胶乳水泥的13%和26.7%的强度。
Adding to early strength agentia and increasing the content of styrene in SBRL can increase the strength of 13% and 26.7%.
普通硅酸盐,回转窑早强型水泥。
Ordinary Silicate Rotary-kiln Producing Early-consolidation Cement.
普通硅酸盐,回转窑早强型水泥。
Ordinary Silicate Rotary-kiln Producing Early-consolidation Cement.