结果表明:PVC的拉伸屈服强度随外力作用速度的提高而提高,断裂伸长率却随之下降。
The results showed that with the the increase of outside force velocity, the tension yield strength of PVC increased, but its breaking elongation decreased.
拉伸强度呈下降趋势,而拉伸断裂伸长率以及冲击韧性则呈先增大后减小的变化趋势,弯曲性能对温湿度交变的环境不敏感。
Tensile strength decreased, while the tensile break extension percentage increased first and then decreased, flexural properties was not sensible to the changing humiture.
随着ATH含量的增加,LLDPE/EVA共混物的拉伸强度逐步增加,断裂伸长率迅速下降。
The tensile strength for LLDPE/EVA blends increases as ATH content is increased, but elongation at break decreases.
结果表明:随着填充油用量的增加,拉伸强度下降,弹性回复增加,断裂伸长率也增大。
The results indicated that with the increase of the content of the extender oil, the tensile strength decreased, while the elasticity increased and elongation at break improved.
经C路径的二次ECAE加工后试样为各向同性材料,其缺口冲击强度较PP有所提高,拉伸强度下降,断裂伸长率提高,表现出很好的延伸性。
The specimen by route C ECAE processing was isotropic and its impact strength increased, tensile strength decreased, elongation at break improved and show…
添加黑液干粉的复合材料,在热氧老化后拉伸强度和邵尔A型硬度增加,断裂伸长率稍有下降。
In general, the tensile strength and Shore A hardness of PVC/CPE/black liquor powder composites were increased while the elongation at break was slightly decreased after thermo-oxidative aged.
三种双醛淀粉膜均随淀粉氧化度的增加拉伸强度(TS)上升,断裂伸长率(E)下降的趋势。
The tensile strengths (TS) of the three DSF increased with the increasing of oxidation extent, while the elongations at break (E) reduced.
结果表明,随应变率的增加,抗拉强度与屈服强度总体呈上升趋势,而断裂伸长率及强塑积单调下降。
The results show that tensile strength and yield strength increase generally, while total elongation and product of strength and ductility decrease with the increase of strain rate.
结果表明,随着PV A吹塑薄膜含水率的增加,其拉伸强度下降,但断裂伸长率增加。
Results showed that the tensile strength decreased with increasing water contents in the film, but at the same time elongation at break was raised.
结果表明,随着PV A吹塑薄膜含水率的增加,其拉伸强度下降,但断裂伸长率增加。
Results showed that the tensile strength decreased with increasing water contents in the film, but at the same time elongation at break was raised.