以混合聚醚多元醇、甲苯二异氰酸酯为主要原料,环氧树脂、羟基丙烯酸树脂为改性剂合成了湿固化聚氨酯涂饰剂。
The moisture cured polyurethane was synthesized with mixing polyether diol, toluene diisocyanate (TDI) as main raw materials, epoxy resin and hydroxy acrylic resin as modifiers.
纤维素纤维改性剂CM系由叔胺与环氧氯丙烷合成。
Modifier CM is synthesised by tertiary amine and epoxy chloropropane for improving properties of cellulose fibre.
概述了国内外PVC 抗冲改性剂MBS的生产现状,不同牌号MBS产品的主要性能、用途,以及MBS树脂的新型合成技术和发展趋势。
This paper introduces the production and application status of MBS resin for PVC, the main character and use of different type MBS resin, newer synthetic technology and development trend.
此种新开发的脲醛树脂,采用特定的先进合成工艺和加入两种改性剂研制而成。
The new urea formaldehyde resin for plywood was developed, by using a specifically designed, advanced synthesis process with two modifiers added in its final stage.
使用一种改性剂XPY,在酚醛树脂的合成过程中成功引入了聚苯醚,制得了一种新的改性环保型酚醛塑料。
Polyphenylene oxide was successfully added to phenolic resin during the syn- thesis process by using a modifying agent XPY, and a new modified environmental phenolic plastic was made.
介绍了目前耐热改性剂pmi的各种合成方法,认为以无机盐或有机盐和有机酸为催化剂的合成方法较佳。
A variety of synthetic methods of heat-resisting modifier PMIare introduced and the use of inorganic, organic salt and organic acid as catalyst is concluded.
应用胶体理论,在树脂合成过程中期加入改性剂,改性剂添加量为3%,合成了性能良好的低毒改性脲醛树脂胶。
Modifier was added on medium-term of synthetic process with its adding amount being 3%, a favourable low toxic modified UF resin adhesive could be synthesized on the basis of colloid theory.
在己内酰胺水解聚合时加入一定量的可反应型复合胺类改性剂,合成出含有胺类改性剂的尼龙6树脂。
Reactive compound amine modifiers were introduced during the polymerization of caprolactam and the nylon 6 with amine modifiers modified was obtained.
综述了近20年来涤纶染色改性剂间苯二甲酸二甲酯- 5 -磺酸钠(SIPM)合成研究进展。
The research progress in synthesis of sodium dimethyl isophthalate-5-sulfonate (SIPM), a dye modifier for PET fibers, was reviewed in recent 20 years.
本文主要介绍PVC新型改性剂as树脂的合成方法、产品性能及其在PVC异型材、管材、注射、压延片等加工领域中的应用。
As resin, as a new modifier for PVC, was synthesized. Its properties and applications in PVC profiles, pipes, injection mouldings, and calendered films were presented.
结果显示,选用改性剂的粘度变化规律符合预期目的,属优等改性剂,这为温拌沥青的最终合成提供了保障。
The results show that the viscosity modifiers selected are consistent with the intended purpose, belonging to the excellent modifiers, which could guarantee the ultimate synthesis of WMA.
通过对脲醛树脂的合成改性,降低了树脂中游离甲醛含量,减小了毒性,加入改性剂后增加了树脂韧性。
Free formaldehyde content in resin is reduced through beetle modification, and the toxicity is thus reduced. The toughness of resin has been increased after adding modifier.
通过对脲醛树脂的合成改性,降低了树脂中游离甲醛含量,减小了毒性,加入改性剂后增加了树脂韧性。
Free formaldehyde content in resin is reduced through beetle modification, and the toxicity is thus reduced. The toughness of resin has been increased after adding modifier.