按此控轧控冷工艺能生产出高等级优质钢筋。
High grade and high quality reinforcing steel bar can be produced according to this control rolling and cooling process.
上述结论为X80管线钢控轧控冷工艺制定提供依据。
The conclusions provide the basis to controlled rolling and controlled cooling of X80 pipeline steel.
通过控轧控冷工艺提高了带钢综合性能,节约了生产成本。
Adoption of the CRCC process improves the general property of strips and reduces the production cost.
用金相方法观察了采用临界奥氏体控轧控冷工艺生产的带肋钢筋的组织及其分布。
The microstructure and its distribution of ribbed bar, produced by critical austenite control rolling and control cooling, were observed by means of microscope.
结果表明,在具有低温轧制能力的高线轧机生产线上,采用控轧控冷工艺生产高强度钢筋是可行的。
The result shows that production of high strength screw bars is reasonable by the control rolling and control cooling process on high-speed wire mill with the capacity of low temperature rolling.
宝钢车轮用热轧酸洗钢带是采用控轧控冷工艺生产的具有优良冷成形性能和焊接性能的低碳微合金化钢。
Hot-rolled pickled steel for automotive wheel is low carbon micro-alloyed steel with excellent properties of cold forming and welding produced by using advanced TMCP technology.
利用微合金化技术及ASP连铸连轧工艺和控轧控冷工艺,济钢自主研发了S450热轧管线钢带产品。
S450 hot rolled strips for line pipe is researched and developed through the technology microalloying, ASP and the processes of controlled rolling and controlled cooling in Jinan Iron and Steel co.
介绍了控制轧制技术在小型材生产中的应用,以及几种典型的控轧控冷工艺布置,可为小型生产厂家提供参考。
Its application in the small section production was introduced. Meanwhile, several types of processing arrangement were put forward, which are references for small section production industries.
在热模拟试验机上研究了控轧控冷工艺对微合金化低碳贝氏体型非调质钢组织性能的影响,并探讨了贝氏体转变机制问题。
The effect of TMCP parameters on microstructure and property was studied, and a controversial question about bainite transformation mechanism also was discussed.
对舞钢采用控轧控冷工艺生产的低碳微合金钢的组织形貌及其形成条件进行了分析,认为组织细化是保证低碳微合金钢良好强韧性配合的重要因素。
The microstructure characteristic and its forming conditions of the low-carbon microalloyed steels were analysed, which were produced by controlled rolling and cooling in Wuyang Iron and Steel Co Ltd.
结果表明,控轧控冷代替常规轧后回火工艺的途径是可行的,并有力地支持了粒状贝氏体的扩散型长大学说。
The replacement of tempering after rolling with TMCP for bainite transformation in SBL steel is a kind of diffusion type.
结果表明,控轧控冷代替常规轧后回火工艺的途径是可行的,并有力地支持了粒状贝氏体的扩散型长大学说。
The replacement of tempering after rolling with TMCP for bainite transformation in SBL steel is a kind of diffusion type.