总的来说，混合废旧塑料制备的复合材料的力学性能要低于纯塑料混合物制备的复合材料，尤其是拉伸断裂伸长率。
In General, the mechanical properties of composites made from recycled plastic blends were inferior to those made from virgin plastic blends, especially in elongation break.
拉伸强度呈下降趋势，而拉伸断裂伸长率以及冲击韧性则呈先增大后减小的变化趋势，弯曲性能对温湿度交变的环境不敏感。
Tensile strength decreased, while the tensile break extension percentage increased first and then decreased, flexural properties was not sensible to the changing humiture.
织物传送带。全厚度拉伸试验。第1部分：拉伸强度、断裂伸长率和标准负荷下伸长率的测定。
Textile conveyor belts - Full thickness tensile testing - Part 1: determination of tensile strength, elongation at break and elongation at the reference load.
并且随着MTES量的增加，材料的拉伸强度增强而断裂伸长率逐渐降低。
Increase in the amount of MTES increases the tensile strength and decreases the ratio of elongation for breaking of the materials.
结果表明：PVC的拉伸屈服强度随外力作用速度的提高而提高，断裂伸长率却随之下降。
The results showed that with the the increase of outside force velocity, the tension yield strength of PVC increased, but its breaking elongation decreased.
对试样进行了硬度、拉伸强度、断裂伸长率、热老化等性能试验；对老化后的试样表面进行了SEM表征。
Hardness, tensile strength, breaking elongation ratio and aging property of samples were tested and surface of sample after aging was represented by SEM.
产品具有突出优点，耐酸、耐碱、耐油、耐寒、拉伸强度高和断裂伸长率等良好的性能。
Product has outstanding advantages, acid, alkali, oil, cold, high tensile strength and elongation at break, good performance.
研究结果表明，浆膜断裂伸长率和断裂比功大的。拉伸模量小的浆料上浆的浆纱耐磨性较好，织造性能也较比良。
Results show that yarns sized by sizes with films of higher breaking elongation and specific work of rupture and lower initial modulus have better abrasive resistance and weaving performance.
竹浆纤维除断裂伸长外。其各项拉伸断裂力学性能指标均远远低于竹原纤维。
In addition to bamboo fiber elongation, but its tensile mechanical properties were far below the bamboo fiber.
有效硫化体系的断裂伸长率、拉伸强度、撕裂强度、耐磨性、抗热氧老化性能最好。
The elongation at break, tensile strength and tearing strength of the HVSSBR cured with EV system are the best.
紫外光加速老化过程中试样拉伸强度、断裂伸长率随组成、光照时间的变化关系；
The relationships of the tensile strength and elongation at rupture and with composition and lighting duration of PE plastics filled with starch were also discussed.
随着ATH含量的增加，LLDPE/EVA共混物的拉伸强度逐步增加，断裂伸长率迅速下降。
The tensile strength for LLDPE/EVA blends increases as ATH content is increased, but elongation at break decreases.
研究了碳纳米管的加入量与分散程度对复合材料的拉伸强度、拉伸模量、断裂伸长率的影响。
The effects of the content and dispersion of carbon nanotubes on the tensile strength, tensile modulus and ratio of elongation of the nanocomposites were studied.
本文比较了涤纶长丝的单丝拉伸与复丝拉伸的断裂强度、断裂伸长及分布和初始模量。
The paper studied difference of mechanical properties between single fiber drawing and multifil drawing of PET filament.
结果表明：随着填充油用量的增加，拉伸强度下降，弹性回复增加，断裂伸长率也增大。
The results indicated that with the increase of the content of the extender oil, the tensile strength decreased, while the elasticity increased and elongation at break improved.
结果发现，在尼龙6中添加pamam后，尼龙6的拉伸强度、断裂伸长率、缺口冲击强度及熔体流动速率均有所提高，PAMAM添加量为1.0%时效果最佳。
The results show that the tensile strength, breaking elongation, impact strength and MFR of nylon 6 increase simultaneously after some PAMAM were added. The optimum increment is 1.0%.
用其改性生产的透明LLDPE专用料的雾度降至11%以下；膜的拉伸强度、断裂伸长率亦有所提高。
The haze of the LLDPE film modified by YS-1 was less than 11% , and the tensile strength and elongation at break of the modified film were all increased.
拉伸强度和断裂伸长率均随辛醛含量的增加而降低。
The results showed that with increasing content of TPU, elongation at break and notched impact strength of the blends increased.
经C路径的二次ECAE加工后试样为各向同性材料，其缺口冲击强度较PP有所提高，拉伸强度下降，断裂伸长率提高，表现出很好的延伸性。
The specimen by route C ECAE processing was isotropic and its impact strength increased, tensile strength decreased, elongation at break improved and show…
对断裂伸长率的影响依次为拉伸倍率、纺速、DF3出口温度。
The results showed the influence on fiber strength and elongation at break was in draw ratio, spinning speed, DF3 exit temperature order.
三种双醛淀粉膜均随淀粉氧化度的增加拉伸强度（TS）上升，断裂伸长率（E）下降的趋势。
The tensile strengths (TS) of the three DSF increased with the increasing of oxidation extent, while the elongations at break (E) reduced.
本发明的产品的拉伸强度和断裂伸长率高、成本低廉、具有可生物降解性。
The production of this invention has high tensile strength and extension at break, costs little, and is biodegradable.
增韧尼龙1 2 1 2的冲击强度大幅提高，断裂伸长率也有提高，拉伸强度并未显著降低。
After toughened, the impact strength of nylon 1212 was increased remarkably, the elongation was also increased, and tensile strength was not decreased too much.
结果表明，随着PV A吹塑薄膜含水率的增加，其拉伸强度下降，但断裂伸长率增加。
Results showed that the tensile strength decreased with increasing water contents in the film, but at the same time elongation at break was raised.
用于织物的抗拉伸断裂强力及断裂伸长的测定。
Model YG 026T Electronic Table Fabric Strength Tester is used for testing the breaking strength and breaking elongation.
力学性能测试结果表明，加有pva的PE防雾膜在拉伸强度，直角撕裂强度，断裂伸长率等方面比未加PVA的防雾膜要小，但不影响其使用性能。
The mechanical experimental results showed that PVA had a little effect on the tensile strength, right Angle tear strength and elongation at break, and...
结果表明：随温度升高，定向有机玻璃的拉伸强度和拉伸模量降低，断裂伸长率增加，材料由刚而脆变得软而韧。
The result shows with the temperature increasing, tensile strength and modulus decreases but elongation increase and material properties change from rigidity to flexibility.
通过测试环向拉伸强度，双向自增强PEX管材的拉伸强度最高可达到32.29%，弹性模量最大可提高13.06%，断裂伸长率平均减小5.88%。
The result reveals that the biaxial oriented PEX pipe can increase the tensile strength by 32.29% at most, while the modulus of elasticity increasing 13.06% and the elongation at break reducing 5.88%.
通过测试环向拉伸强度，双向自增强PEX管材的拉伸强度最高可达到32.29%，弹性模量最大可提高13.06%，断裂伸长率平均减小5.88%。
The result reveals that the biaxial oriented PEX pipe can increase the tensile strength by 32.29% at most, while the modulus of elasticity increasing 13.06% and the elongation at break reducing 5.88%.