合金元素和工艺因素都会影响微观偏析。
All alloy elements and process factors can influence the micro-segregation.
与其它合金一样,铸铁的偏析也分宏观偏析和微观偏析。
As that of other alloys, the segregation of the cast iron is also divided into macro-segregation and micro-segregation.
利用激光快速熔凝技术对DD 2单晶合金在超高温度梯度和快速凝固条件下的组织形态和元素的微观偏析行为进行了研究。
The microstructure characteristics and microsegregation of DD2 single crystal have been studied under ultra-high temperature gradient and rapid solidification conditions by laser rapid remelting.
结果表明,微观组织无明显偏析,连铸工艺参数选择不当是X65出现裂纹的主要原因。
The results show that obvious segregation is not found in the microstructure and the main reason appeared crack in X65 steel is improper process parameters during the continuous casting.
结果表明,微观组织无明显偏析,连铸工艺参数选择不当是X65出现裂纹的主要原因。
The results show that obvious segregation is not found in the microstructure and the main reason appeared crack in X65 steel is improper process parameters during the continuous casting.