再结晶是形变组织球化过程的必要条件。
Recrystallization is the necessary condition for spheroidization of the deformed texture.
研究热形变过程激活能和应力指数与形变组织的关系。
The dependence of activation energy and stress exponent upon the structure state is elucidated.
研究了高锰奥氏体钢在77K下的抗拉性能、形变组织和断裂特点。
The tensile properties, deformed microstructure and fracture at 77K in high-Mn austenitic steels have been investigated.
谭雅：你说最常见的损伤实际上是机体组织形变，对吗？
Tanya: And you say that the injuries that are most common that you see are orthopedic in nature. Is that right?
总结了一些微量元素和痕量元素对形变铝合金组织、性能的影响。
The effects of some trace elements on structures and properties of wrought aluminium alloys are summarized.
利用SEM、TEM研究了同一成分的热轧双相钢的马氏体体积分数对形变位错结构和断口组织特征的影响。
Effect of martensite volume fraction on deformation dislocation structure and fracture for hot rolled dual-phase steel of the same composition was studied by using SEM and TEM.
结果表明，伴随着组织的变化，织构的类型也由形变织构变为典型的再结晶织构，且再结晶织构形成机制符合择优生长理论。
The results show that the deformation textures are turned into recrystallization textures and the mechanism of this change accords with oriented growth theory.
软组织的形变信息是通过超声回波延迟时间得到的。
The deformation information is obtained from ultrasonic echo time delay.
采用TEM对形变位错密度以及马氏体组织进行了分析。
The deformation dislocation density and martensite microstructure were also analysed by TEM.
原始材料的组织状态为形变马氏体、淬火马氏体及残余奥氏体。
The original structure consists of deformation induced martensite, quenching martensite and retained austenite.
综述了几种原始组织的材料表面形变强化的有效性，讨论了三个主要因素的作用和相互关系。
This review attempts to discuss the effectuality of surface plastic deformation strengthening treatment and the role of main influential factors for different original microstructure of steels.
等温温度和保温时间是形变镁合金组织球状化的两个重要控制因素。
When the preformed Magnesium alloy's texture was globalizing, there were two important control factors, which were holding temperature and holding time, affecting the globalization processing.
采用形变热处理工艺，使工业用LF 6合金板材得到细小、等轴的晶粒组织。
A kind of fine and equiaxed crystal structure of LF6 aluminum alloy plate material is obtained by means of the technique of deformation heat treatment.
形变使奥氏体中温转变产物岛状组织数量增加，并使之细化。
The deformation increases quantity of island structure in the product of medium temperature transformation in austenite and makes it finer.
本文研究了热处理对冷加工奥氏体不锈钢组织的影响，试验结果表明利用形变马氏体的逆转变可获得超细化不锈钢晶粒。
The experimental results show that ultrafine grained austenitic stainless steel can be obtained by the reversal transformation of deformation-induced martensite.
研究了AZ 91d镁合金在应变诱发熔化激活法处理过程中形变率和形变温度对组织的影响。
The influences of strain and temperature on microstructure of AZ91D alloy for upsetting in the strain-induced melt activation process were investigated.
用金相显微镜及X射线衍射仪对形变含稀土低碳钢热浸镀铝的镀层微观组织进行了分析，并探讨了其形成机制。
The microstructure of hot-dip aluminum coat of deformed low-carbon steel containing RE has been analyzed by metallography microscopy and XRD, and the forming mechanism has also been discussed.
随着切削速度的提高，绝热剪切带的显微组织发生了由形变带向转变带的演变。
The deformation bands change into the transformation bands in microstructure as the cutting speed increases.
模型把子区域地形几何数据定义为单纯复合形集，按地形变化时间顺序和空间关系组织成一个偏序集。
The model is based on a collection of a divisional terrain data defined as simplicial complexes arranged into a partially ordered set by time and space.
碳化物的析出量主要由形变温度和该形变温度下热变形奥氏体的组织状态决定。
The amount of carbides depends on deformed temperature and microstructure of austenite at thermally deformed at the deformed temperature.
通过热模拟实验，考察了在不同变形温度和不同奥氏体晶粒尺寸等条件下保温对低碳钢形变后组织演变的影响。
The influence of deforming temperature as well as primal austenite grain sizes and holding time on the microstructure of transformation were investigated.
结果表明，形变诱发马氏体组织所加剧的加工硬化与冶炼时所产生的气孔缺陷的共同作用是冷轧断带的原因。
The results show that the effects of work hardening by strain-induced martensite transformation and cast pore defects are the main reasons leading to strip broken of the steels during cold rolling.
锯齿形切屑中存在两种形式的绝热剪切带，没有组织转变特征的形变带和组织明显细化的转变带。
There are two forms of adiabatic shear bands in the sawtooth chips, which are deformation bands with no organizational change and transformation bands with obvious organizational refinement.
研究了SS400低碳钢在中高温形变及形变后停留时显微组织的变化。
Deformation and microstructure change of SS400 low carbon steel at middle and high temperature, different holding times after deformation were investigated.
采用力学性能测试、金相显微分析和TEM等方法。研究了形变热处理工艺对7a04铝合金的组织和性能的影响。
The effects of thermomechanical treatment on the structures and properties of 7a04 aluminum alloy were studied by mechanical tensile test, metallographic and TEM analysis.
本文对超塑性形变过程中的组织变化进行了研究。
In this paper, The Microstructure of hard-Aluminum Alloy LY12 in superplastic deformation is studied.
分析了退火对热成形组织及织构的影响，确定了< 110 0 >织构的消失与残余形变晶粒再结晶的联系。
The vanishing of texture during annealing was related with the recrystallization in deformed elongate grains which survived the hot extrusion.
分析了退火对热成形组织及织构的影响，确定了< 110 0 >织构的消失与残余形变晶粒再结晶的联系。
The vanishing of texture during annealing was related with the recrystallization in deformed elongate grains which survived the hot extrusion.