结果表明；随着烧结温度的升高，开口气孔率降低，断裂强度升高。
Results show that the open porosities are decreased and fracture strength is increased with the increase of the sintering temperatures.
炭滑板经浸渍金属后，致密性、抗折强度、抗压强度、肖氏硬度明显提高，而开口气孔和电阻率降低。
The compactness bending strength, compressive strength, shore-hardness of carbon slides impregnated with metals were increased; while open porosity and electrical resistivity decreased.
炭滑板经浸渍金属后，致密性、抗折强度、抗压强度、肖氏硬度明显提高，而开口气孔和电阻率降低。
The compactness bending strength, compressive strength, shore-hardness of carbon slides impregnated with metals were increased;
样品内部均匀分布了大量的开口气孔和闭口气孔，样品均匀分布的闭气孔不仅降低了样品的吸水率，而且增加了样品的抗冻融性。
There are evenly distributed open pores and closed pores Inside sample, evenly distributed closed pores not only reduce the Wa, but also increase the resistance to freezing and thawing.
样品内部均匀分布了大量的开口气孔和闭口气孔，样品均匀分布的闭气孔不仅降低了样品的吸水率，而且增加了样品的抗冻融性。
There are evenly distributed open pores and closed pores Inside sample, evenly distributed closed pores not only reduce the Wa, but also increase the resistance to freezing and thawing.