表明口模拉伸过程中既存在应力诱导的结晶过程，又存在温度诱导的二次重结晶过程。
It is showing where is either the crystallizing process by the stress introducing or secondary crystallizing process by the temperature introducing.
结果表明，该共混体系中界面应力的应变诱导致结晶作用及其所引起的基体中伸展链晶体网络结构的形成是该材料实现脆韧转变的重要原因。
The results show that the interfacial stress produced from the shrinkage of the matrix in the composites injection molding process can strain induced crystallization of th.
结果表明，该共混体系中界面应力的应变诱导致结晶作用及其所引起的基体中伸展链晶体网络结构的形成是该材料实现脆韧转变的重要原因。
The results show that the interfacial stress produced from the shrinkage of the matrix in the composites injection molding process can strain induced crystallization of th.