结果表明，试验件含分层损伤面积越大，其破坏载荷越大，而对应的破坏应变越大，因此分层损伤会降低复合材料层合板的承载力和刚度。
The results of experimentation indicate that the failure load of the delaminated composite panels declines and the failure strain increases as the increasing of delaminated area.
结果表明，试验件含分层损伤面积越大，其破坏载荷越大，而对应的破坏应变越大，因此分层损伤会降低复合材料层合板的承载力和刚度。
The results of experimentation indicate that the failure load of the delaminated composite panels declines and the failure strain increases as the increasing of delaminated area.