开展油田钻柱失效分析与预防对提高钻井速度、降低钻井成本及井下安全钻进具有重要意义。
It is very important for improving drilling rate, reducing drilling cost and safety drilling to carry out drill stem failure analysis and prevention.
对定向凝固合金叶片的裂纹进行分析，在断口观察与金相组织分析的基础上，对叶片的失效模式与失效原因进行研究，并提出预防该类故障发生的措施。
The cracks on blades made of a directionally solidified superalloy were analyzed. The failure mode and cause were studied in virtue of fracture observation and metallographic analysis.
对定向凝固合金叶片的断裂故障进行了分析，在断口观察与金相组织分析的基础上，对叶片的失效模式与失效原因进行了研究，并提出了预防该类故障发生的措施。
The fracture of blades made of a directionally solidified superalloy was analyzed. The failure mode and cause were studied in virtue of fracture observation and metallographic structure analysis.
对定向凝固合金叶片的断裂故障进行了分析，在断口观察与金相组织分析的基础上，对叶片的失效模式与失效原因进行了研究，并提出了预防该类故障发生的措施。
The fracture of blades made of a directionally solidified superalloy was analyzed. The failure mode and cause were studied in virtue of fracture observation and metallographic structure analysis.