结果证明,不同质量的坩埚会对基线产生不同的影响,并进一步影响到试验数据的分析。
The results showed that crucibles with different qualities can result in different baseline to further influence the analysis of experimental data.
在竖管炉中用石墨坩埚进行还原试验。
Reduction experiments have been conducted in a vertical tube furnace using graphite crucible.
该模具组件由熔化坩埚部件和流动性试验部件两部分组成。
The mould component is composed of a melting crucible part and a mobility test part.
工作试验结果表明,新材质制造的坩埚使用寿命是普通铸铁坩埚的2—3倍。
The industrial tests have shown that the service life of new alloy cast iron crucible is 2-3 times as long as ordinary grey cast iron crucible.
独特设计,检测热电偶可放置在坩埚正中,能有效的控制试验过程最后7分钟的样品温度。
TEMPERATURE MONITORING SYSTEM: As needed, with a thermocouple placed at the crucible, temperature can be monitored to obtain a constant temperature during the last 7min of process.
工业试验结果表明,新材质制造的坩蜗使用寿命是普通铸铁坩埚的2 ~3倍。
The industrial test results have shown that the service life of new low alloy cast iron crucible is 2-3 times as long as ordinary grey cast iron crucible.
本文介绍了“舟型浅槽六排孔短漏板”坩埚拉丝试验的主要情况及经济效益分析。
This paper introduces the main conditions and economic results of fiber drawing tests of boat - shaped shallow and short bushing with 6 rows of nozzles.
试验以预处理的FCC 油浆为原料,采用程序升温、多管井式坩埚炉进行热转化形成有序生长中间相反应研究。
Orderly growth of mesophase was studied using FCC slurry as raw materials, in a multi-tube well-crucible furnace controlled by programmed heating.
试验以预处理的FCC油浆为原料,采用程序升温、多管井式坩埚炉进行热转化形成有序生长中间相反应研究。
Orderly growth of mesophase was studied using FCC slurry as raw materials, in a multi-tube well-crucible furnace controlled by programmed heating.
试验以预处理的FCC油浆为原料,采用程序升温、多管井式坩埚炉进行热转化形成有序生长中间相反应研究。
Orderly growth of mesophase was studied using FCC slurry as raw materials, in a multi-tube well-crucible furnace controlled by programmed heating.