在含碳量1.5%的铁基体中主要沿晶界分布;在含碳量3%的基体中呈均匀分布。
In composites contained 1.5%C, VC particles were along austenite crystal boundary, while others of 3%C content were distributed uniformly.
这是由于变形不均匀和晶界上析出的平衡脆性相耦合作用的结果。
This is due to the coupling of inhomogeneous deformation and the brittle equilibrium phase on the boundary.
结果显示,杂质元素的含量偏高和沿晶界的偏析以及不均匀的钨晶粒是造成国产钨靶表面损伤的主要原因。
The results show that high content of impurity elements, segregation along grain boundaries and uneven grain size are main reasons for the surface damage of domestic tungsten targets.
路基、地基的不均匀沉降问题一直是岩土工程界的一个重要研究内容。
The uneven settlement of highway foundation is always of great concern in the field of geotechnical engineering.
本文研究了热形变工艺参数对奥氏体晶界和晶内不同区域的形变程度不均匀性的影响。
This paper researches the influence of technology parameters of hot deformation on the nonhomogeneous deformation between the austenitic grains and different zones within the grains.
分析结果表明,铸锭中分布不均匀的非金属夹杂物和组织中过量分布于晶界的贝氏体和三次渗碳体是导致冷镦开裂的原因。
It was revealed that: inhomogeneous distribution of the non-metallic inclusion and excessive bainite and tertiary cementite is the cause of cracking.
毛细孔分布均匀、孔径适宜、韧度高、耐油性高、不易腐蚀、容易清洗干、不易变色、性质温和柔软,是美容界认定的一种高级产品。
They are thought as high quality products for their densities are well distributed; aperture is proper, high ductile, high oil resistance, not easy to corrode and fade away, easy to wash and soft.
我们还说明了通过外加一个非均匀的磁场可以使得通过磁性光子晶体的电磁波束弯曲,从而产生类似于自然界中海市蜃楼的现象。
We also demonstrated the possibility of molding the flow of em beam in the magnetic photonic crystal with a nonuniform ESMF to create a mirage effect.
人参乌龙茶外形如图,颗粒大小适中、均匀圆润,颜色鲜绿,其外形可以说是茶界中的“第一美茶”。
Ginseng Oolong tea form shown, the particle size is moderate, evenly rounded, bright green color, its shape can be said that in the tea sector, "the first U."
结果表明:所制备的样品为纯相,样品颗粒度均匀,晶界清晰,品质较高;
The results indicated that: The prepared sample is pure phase, the sample particle size uniformity, grain boundary clear of higher quality;
结果显示,杂质元素的含量偏高和沿晶界的偏析以及不均匀的钨晶粒是造成国产钨靶表面损伤的主要原因。
The results show that high content of impurity elements, segregation along grain boundaries and uneven grain size are main reasons for the surface damage of domestic tung...
结果显示,杂质元素的含量偏高和沿晶界的偏析以及不均匀的钨晶粒是造成国产钨靶表面损伤的主要原因。
The results show that high content of impurity elements, segregation along grain boundaries and uneven grain size are main reasons for the surface damage of domestic tung...
应用推荐