进行高温均匀化处理促使粗大第二相质点溶入基体。
High temperature homogenizing treatment prompts the coarse second phase particle to dissolve into the matrix.
分析铸态组织后，将试样进行不同程度的均匀化处理。
The samples were heated in different extent of homogenization after analyzing the as-cast microstructure.
因此，电场及非电场的联合处理方法是一个有效的均匀化处理制度。
Therefore, the combined homogenization treatment with and without an electric field is an effective method of homogenization treatment.
研究了均匀化处理、固溶时效、冷变形时效等对铬青铜显微组织和性能的影响。
The microstructure and properties of chromium bronze after homogenizing treatment, solid solution and aging treatment, cool deformation and aging was studied.
系统研究了5083合金铸锭均匀化处理和不均匀化热处理对铸锭、成品板材组织和性能的影响。
The effects of 5083 aluminium alloy ingot homogenizing and non-homogenizing on properties and structures of ingot and plates are researched.
对IN706合金的均匀化处理工艺进行了探索，同时研究了均匀化处理对材料热加工性能的影响。
The homogenizing treatments and it 's effect on hot workability of IN706 alloy was studied in this paper.
研究了热处理工艺（包括均匀化处理、淬火方式和人工时效等）对6063铝合金组织和力学性能的影响。
The effect of heat treatment(including homogenizing treatment, quenching method and artificial aging)on the structure and mechanical property of 6063 aluminum alloy was studied.
球经高频低压等离子体浸没离子注入及氮化处理后，样品表面的硬度、耐磨性和耐腐蚀性显著提高，具有较好的均匀性。
The hardness, wear resistance and corrosion resistance of the ball were significantly increased after the treatment of HLPIII, and had better uniformity.
钢丝经磷化处理，且磷化层均匀， 一致。
The wire have been phosphate coated and uniformly , coincidently.
在SEM下观察发现，钝化处理后镁粒表面生成了致密的钝化层，且包裹均匀。
It is founded under SEM that the passivated coating of magnesium powder is compact and even.
与常规晶化相比，快速晶化处理的薄膜结晶质量好，晶粒较小、分布均匀致密。
Compared with conventional furnace annealing, PbTiO3 thin films by rapid thermal annealing had smaller, denser and uniform crystal grains in size with better crystallographic quality.
本文是对铬钨锰钢进行碳化物细化处理和不均匀奥氏体淬火的试验研究结果。
This is the result on studying carbide refining treatment and non-uniform austenite quenching.
熔体熔化处理后，搅拌均匀，取样分析。
The melt after melting treatment, mixing evenly, the sample analysis.
常化处理使组织均匀化并增加有利于磁性提高的织构组分；
Normalizing treatment makes microstructure uniform and increases component of favorable texture.
而浸渍树脂的碳毡硅化处理后的显微组织特点是反应生成的碳化硅颗粒粒径及分布均不均匀。
As for the impregnated carbon felt, the reaction-formed SiC particles were nonuniform in size and distribution, and the smaller SiC particles would dissolve with the increase of sintering time.
而浸渍树脂的碳毡硅化处理后的显微组织特点是反应生成的碳化硅颗粒粒径及分布均不均匀。
As for the impregnated carbon felt, the reaction-formed SiC particles were nonuniform in size and distribution, and the smaller SiC particles would dissolve with the increase of sintering time.