结果表明：多重固溶时效热处理可以显著提高合金的塑性和断裂韧度，而对强度的影响不大。
The results showed that multiple solution and aging treatment had a significant effect on increasing plastic property and fracture toughness, although had little effect on strength.
结果表明，退火态2224铝合金经e CAP挤压后，进行固溶和时效处理，明显提高了合金的力学性能，细化了合金的晶粒。
It is shown that the mechanical properties of annealed sample of 2224 aluminum alloy are improved by the combination of solid solution and aging treatment after ECAP, the size of grain is refined.
经固溶处理和自然时效的铝铜合金可以进行硬质阳极氧化。
Hard anodizing film could be obtained on Al-Cu alloy surface which had been treated with solid solution treatment and natural aging.
研究了经不同的固溶和时效方案处理的7711铝合金的力学性能，并结合微观组织进行了分析。
The mechanical properties of 7711 aluminum alloy under different solution and aging conditions were investigated and analyzed by combining with the microstructure.
介绍了固溶处理温度、淬火到时效间隔时间及时效制度等对2A70铝合金预拉伸厚板组织和性能的影响；
The effect of quenching temperature, the interval time from quenching to aging and aging institution to 2A70 aluminium alloy pre-stretching plate structure and properties are introduced.
研究了均匀化处理、固溶时效、冷变形时效等对铬青铜显微组织和性能的影响。
The microstructure and properties of chromium bronze after homogenizing treatment, solid solution and aging treatment, cool deformation and aging was studied.
固溶时效热处理使压缩吸能能力随着孔隙率的增大而呈现规律性减小，并使能量吸收效率对孔隙率和孔径的敏感程度减小。
The energy absorption capacity decreased regularly along with the increase of porosity and the energy absorption efficiency became insensitive to pore size (d) and porosity (P_r).
固溶时效热处理使压缩吸能能力随着孔隙率的增大而呈现规律性减小，并使能量吸收效率对孔隙率和孔径的敏感程度减小。
The energy absorption capacity decreased regularly along with the increase of porosity and the energy absorption efficiency became insensitive to pore size(D) and porosity(P…
固溶时效热处理使压缩吸能能力随着孔隙率的增大而呈现规律性减小，并使能量吸收效率对孔隙率和孔径的敏感程度减小。
The energy absorption capacity decreased regularly along with the increase of porosity and the energy absorption efficiency became insensitive to pore size(D) and porosity(P…