分析了不锈钢压力表管接头焊缝开裂的原因，认为此种开裂具有应力腐蚀开裂、沿晶断裂特征。
The rupture reasons of tube joint weld of the stainless steel pressure meter are analyzed. It is characteristic of stress corrosion cracking and inter granular fracture.