通常利用加速腐蚀试验采用失重法表征耐候钢的耐大气腐蚀性能。
Usually, corrosion resistance of weathering steels is evaluated by the weight-loss method in an accelerated corrosion test.
采用模拟和加速腐蚀试验方法，研究了广州地铁工程混凝土对地下水的耐腐蚀性能。
The corrosion resistance of Guangzhou Metro engineering concrete to groundwater was investigated by simulated and accelerated corrosion tests.
采用化学和电化学加速腐蚀试验方法对6种不锈钢的耐点蚀和缝隙腐蚀性能进行了评价。
Using accelerated chemical and electrochemical corrosion testing methods, the resistance to pitting and crevice corrosion behavior for six stainless steels were evaluated.
验收项目中，有一个耐湿试验分组，用来加速评定外壳的抗腐蚀性能及相应的质量可靠性能。
In acceptance tests, a moisture resistance test is used to evaluate the anticorrosion property of the package and its relevant quality reliability.
结果表明该加速腐蚀仪具有良好的可靠性和精度，可用于灌浆料的抗氯离子侵蚀性能的试验研究。
The test results indicate that the apparatus which possess good reliability and precision, can be applied on the study of chloride corrosion of grout.
采用周期浸泡加速试验方法，研究了石粉锂渣超早强超高强混凝土的耐硫酸腐蚀性。
The sulphuric acid erosion resistance of super-early and super-high strength concrete containing limestone powder and lithium slag was studied by means of accelerating cycle soak test.
采用持续753 h的加速试验模拟腐蚀过程。
An accelerating corrosion test last for 753 hours had been finished.
首先用加速腐蚀环境谱对无裂纹试件进行腐蚀试验，然后进行拉伸超载疲劳试验。
The tension overload fatigue tests are carried out, which are corroded under the accelerated corrosion environment in this paper.
以45钢、A3钢、炮钢、20钢为金属试样，研究它们在中性盐雾加速试验及石家庄大气环境暴露试验中腐蚀失重与时间的变化规律。
The correlativity between neutral salt spray accelerated test and atmospheric corrosion test in Shijiazhuang was studied by the mass loss determination of 45 steel, A3 steel, 20 steel and gun steel.
将黄铜片用上述三种溶液钝化处理后，通过湿热加速试验、硝酸点滴试验、盐水浸泡试验及电化学测试对耐腐蚀性进行了研究。
The corrosion resistance of samples after passivation is studied in the experiment by humid-air accelerated corrosion test, nitric acid titrating test and the brine dipping test.
针对海洋性气候条件下航空铝合金的大气腐蚀，提出了一种综合环境加速试验方法。
Using aeronautical aluminums, the accelerated corrosion tests for Marine atmospheric corrosion were studied, and a comprehensive environmental test was proposed.
采用室内模拟加速试验装置，对紫铜、青铜、黄铜和白铜等几类铜及铜合金，在不同泥沙含量的海水中的冲蚀情况及腐蚀速率进行了研究。
The erosion rate and morphology of nine kinds copper and copper alloy, including brass and bronze, were investigated in sea water with different silt content through indoor simulated tests.
采用室内模拟加速试验装置，对紫铜、青铜、黄铜和白铜等几类铜及铜合金，在不同泥沙含量的海水中的冲蚀情况及腐蚀速率进行了研究。
The erosion rate and morphology of nine kinds copper and copper alloy, including brass and bronze, were investigated in sea water with different silt content through indoor simulated tests.