力学性能检验;
通过对焊接接头的力学性能检验、微观组织观察和分析,证明了该焊接工艺的可行性。
The mechanical property of weld joint was tested and the microstructure was analysed, the welding process was proved feasible.
通过化学成分分析、力学性能测试、金相检验以及断口分析等方法对SKD61钢压铸模具开裂原因进行分析。
The cracking causes of the die casting mould of SKD61 steel were analyzed by chemical composition analysis, mechanical property testing, microstructure examination and fracture analysis.
采用化学成分分析、力学性能测试、显微组织观察和夹杂物检验等方法对有边缘裂纹的Q 345 B宽带钢进行分析。
The edge crack on Q345B wide strip steel was analyzed by means of chemical composition analysis, mechanical property testing, micro metallographical examination.
采用宏微观检验、化学成分分析及力学性能测试方法对截止阀阀体爆裂原因进行了分析。
This paper studied the causes of bursting of stop valve by the methods of visual inspection, metallographical examination, chemical analysis and mechanical property test.
介绍了现在通行的燃料棒辐照后破坏性检验的一般方法,包括燃料辐照后的微观结构观察和力学性能试验;
Several methods of destructive post-irradiation examination(PIE) including microstructure observing and measurement of mechanical properties of irradiated fuel rod were introduced.
采用化学成分分析、宏观和微观组织检验以及力学性能测定等方法对在使用过程中发生开裂的包胶辊进行了分析。
The cracking encapsulated roller in use was analyzed by means of chemical composition, macrostructure and microstructure examination and mechanical property test.
扭转试验在确定材料力学性能、检验材料质量方面被广泛采用。
The experiment of torsion is widely adopted to test the mechanical capability of materials and to check up the quality of materials.
检验评判标准错误导致化学成份不符,力学性能达不到要求。
The error standards of the inspection & judgement caused the non-conformity of chemical ingredients and fails to reach the requirement of mechanical performance.
按照《普通混凝土用碎石或卵石质量标准和检验方法》(JGJ52-2006)测试了由该工艺生产的再生骨料的物理力学性能指标。
Various physical and mechanical properties of RCA from this technology were investigated according to Standard and Test Method for the Coarse Aggregate of Normal Concrete (JGJ 52-2006).
采用化学成分分析、力学性能测定、金相检验以及断口宏、微观分析等方法,对钻井泵齿轮轴断齿进行了分析。
Fracture tooth of gear shaft in well drilling pump was analysed by chemical analysis, mechanical testing metallographic examination macro and microfractography.
采用化学分析、力学性能测试和金相检验等手段,对某电站汽轮机主油泵轴的早期断裂进行了分析。
Chemical composition analysis, mechanical property test and microstructure examination were used to analyze the early fracture of power plant's turbine main oil pump shaft.
通过宏观分析、断口分析、化学成分检验、金相检验和力学性能检测等方法,对汽车发动机曲轴断裂原因进行了分析。
The analysis of automobile engine crankshaft was conducted by macroscopic examination, fracture analysis, chemical composition analysis, metallographic examination and mechanical properties test.
详细介绍了X65卷板的生产流程和有关力学性能(拉伸性能、冲击性能及硬度)的检验结果。
The milling process of X65 pipe steel and the inspection data of mechanical properties (tensile strength, DWTT and hardness)are introduced in detail.
采用金相检验、力学性能测定等方法,对断裂花篮螺杆进行了分析。
The fracture of Turn Buckle was investigated by means of metallography and mechanical testing.
采用化学分析、力学性能试验和金相检验等方法对该裂纹进行了分析。结果表明,此缺陷是由于试验环原始表面的粗糙度过大造成的。
By means of chemical composition analysis, mechanical property test and microstructure examination, the results showed that this defect was result of rough surface and not the crack existed in matrix.
目的检验关于胶原蛋白是皮肤黏弹性主要决定因素的假设,重点考察皮肤组织在动态载荷下的热力学性能。
Objective to test the hypothesis that collagen is a significant determinant of skin viscoelasticity, with particular attention paid to the thermomechanical properties of skin under dynamic loading.
对开裂杯形螺母的力学性能和化学成分进行了检验分析,并进行了工艺试验。结果表明,毛坯尺寸偏短是造成开裂的主要原因。
Through mechanical test and chemical analysis and technological experiment of the cracked cap nut, it was concluded that the short size of nut blank caused surface crack.
采用残余应力和力学性能测定、化学成分分析、断口扫描及金相检验等方法对铁路货车用l - B型组合式制动梁撑杆翼板产生裂纹的原因进行了分析。
The integrated analysis of crack failure for L-B Composite Brake Beam Bar Flange Slab was made by means of SEM, microscope and chemical analysis.
采用残余应力和力学性能测定、化学成分分析、断口扫描及金相检验等方法对铁路货车用l - B型组合式制动梁撑杆翼板产生裂纹的原因进行了分析。
The integrated analysis of crack failure for L-B Composite Brake Beam Bar Flange Slab was made by means of SEM, microscope and chemical analysis.