从混凝土磨蚀和力学性能试验得知,水工混凝土的磨蚀程度依赖于混凝土的初始磨损率,抗拉强度和极限拉伸变形值。
Abrasion and mechanical properties test of concrete have shown that the degree of abrasion dependent on initial abrasion ratio, flexural strength and limit strain.
研究结果表明,采用合理的初始辊形可以一定程度上弥补轧辊磨损和热变形对带钢断面的不良影响,大大优化了带钢断面形状。
Research results show that bad strip profile caused by wear and thermal crown of roller may be properly repaired by sound original roller contour, and strip profile is greatly improved.
系统在初始状态时可以认为被赋予了随机大小的资源,那么系统寿命的消逝过程可以看成是磨损对随机资源的消耗过程。
A system at inception is endowed with a random amount of resource, the process of the lapse of system life can be viewed as that of the depletion of random resource caused by the wear-out effect.
某钢厂转炉炉壳与托圈的联接方式初始设计为悬盘联接,该种联接装置使用一段时间后发现悬盘及悬盘孔的磨损较为严重。
After using this kind of connection equipment for some time, heavy wear was found at pan and the suspending pan hole.
分析结果表明, 纤维切割过程中,切断刀锋利性能的变化主要与切断刀的初始刃口半径、刃口角度、刃口的磨损量以及刃口上缺口的深度有关。
The result shows that the cutter blade edge radius, edge angle, the linear abrasion and the edge notch depth are main factors affecting its sharpness.
结果表明初始焊接阶段电极磨损速率较大,点蚀加剧了电极磨损与失效。
The results showed that electrode wear rate was higher at beginning welds than later welds; pitting building at electrode surface accelerated electrode wear and invalidation.
滚滑条件下,车轮材料应变硬化程度的高低不影响车轮材料的抗磨损性能,试验前车轮材料初始硬度的高低是决定其抗磨损性能的主要因素。
The wear resistance of wheel steels is not affected by strain hardening under rolling/sliding conditions, while it is dominated by the pre-hardness of wheel steels.
滚滑条件下,车轮材料应变硬化程度的高低不影响车轮材料的抗磨损性能,试验前车轮材料初始硬度的高低是决定其抗磨损性能的主要因素。
The wear resistance of wheel steels is not affected by strain hardening under rolling/sliding conditions, while it is dominated by the pre-hardness of wheel steels.