结果表明,高温淬火和分级淬火可使应力腐蚀断裂抚力k _ (ISCC)值得到明显提高。
Results show that both high temperature quenching and step quenching can apparently increase the stress corrosion cracking resistance K_ (ISCC).
采用分级淬火的方法测定了7055铝合金的温度—时间—性能(ttp)曲线,并结合合金实际淬火冷却曲线通过淬火因子分析方法预测了合金的硬度。
Combined with measured cooling curves, the TTP curve was used to predict the influence of quenching rate on the hardness of 7055 aluminum alloy by quench factor analysis method.
采用分级淬火的方法测定了7055铝合金的温度—时间—性能(ttp)曲线,并结合合金实际淬火冷却曲线通过淬火因子分析方法预测了合金的硬度。
Combined with measured cooling curves, the TTP curve was used to predict the influence of quenching rate on the hardness of 7055 aluminum alloy by quench factor analysis method.