对冲击磨损试验后试样进行了失重测量，并用SEM分析磨损表面形貌，用OM观察金相组织。
The mass loss after impact-wearing was measured, the morphology on the wear surface of the steel was analyzed by SEM, the microstructure was observed by OM.
用X射线衍射分析方法测定了镀层表面结构并作了冲击磨料磨损试验。
The X-ray diffraction was used to determine the structure of the coating surface. At last, the shock abrasive wear test was performed.
通过自制的冲击腐蚀磨损试验机，施加不同极化电位对高锰钢在矿浆介质中的冲击腐蚀磨损行为进行了试验研究。
Effect of polarization potential on the corrosion-wear behavior of high manganese steel in ore slurry was investigated by a self-made impact corrosive-wear tester.
结果表明，在中、低冲击磨料磨损条件下，试验钢的耐磨性优于中碳低合金耐磨钢和高锰钢。
Under lower and medium impact energy, the abrasive wear resistant performance of the steel metioned is higher than that of low alloyed medium carbon wear resistant steel and high manganese cast steel.
在改进的MLD - 10型冲击腐蚀磨损试验机上，对不同成分的低碳高合金钢的冲击腐蚀磨损性能进行了测试。
LCHA with several variations of composition were tested with a modified MLD-10 wear tester to investigate their behavior under corrosive impact abrasion.
结果表明，在相同试验条件下低碳高合金钢的冲击腐蚀磨损性能要优于高锰钢的。
The results show that the resistance of low carbon high alloy steel is better than that of the high manganese steel under the same test condition.
在改进的MLD - 10型冲击腐蚀磨损试验机上，选择三种不同的冲击功，对以锰代镍的低碳高合金钢的冲击腐蚀磨损性能进行了测试。
Under three different impact energy, LCHA with Mn in place of Ni were tested with a modified MLD-10 wear tester to investigate their behavior of corrosive impact abrasion.
在动载三体磨粒磨损条件下，试验研究了冲击载荷的变化对铸态复相耐磨钢动载磨粒磨损特性的影响。
The influence of varying impact energy on wear resistance of dual phase cast steel has been investigated under impact three body abrasion.
试验得出，残余奥氏体可阻止疲劳裂纹的萌生和扩展，提高冲击疲劳抗力，降低冲击疲劳磨损。
It is indicated that retained austenite in microstructure can inhibit the initiation and propagation of fatigue crack, improve the resistance to impact fatigue and decrease impact fatigue wear.
用微观组织分析、杆盘式磨损、湿磨法磨损和冲击韧性等试验手段，对高铬铸铁衬板的显微组织、力学性能和耐磨性进行了试验分析。
Failure analysis of high chromium cast iron liner has been studied by the microstructure, pole-pan wear abrasion, wet grinding and impact toughness.
对所研制的高速滚子链进行了常规检测与试验、滚子大能量冲击疲劳试验、滚子链高速运转试验和滚子链磨损试验。
Common measure and experiment, impact fatigue experiment with large energy, revolving experiment at high speed and wear experiment are described in this paper.
硬铸铁和常用的铬系白口铸铁进行了削盘磨损试验和冲击磨料磨损试验。
Abrasion-resistant capability of Ni-cast iron and Cr-cast iron were studied by abrasion wears and impact test.
本文就PC D刀具断续切削铝合金时的切削力、切入冲击力和刀具磨损等问题进行了试验研究。
An experimental study on cutting force, cut - in impact force and cutting - tool wear are conducted in the interrupted cutting of aluminum alloy with PCD tools.
通过落球冲击和滑动磨损试验探讨了冲击对高铬铸铁和奥氏体不锈钢耐磨性的影响。
Effect of impact on wear resistance of high chromium cast iron and austenitic stainless steel has been studied by ball-on-ball impact and pin-on-disc abrasion test.
通过落球冲击和滑动磨损试验探讨了冲击对高铬铸铁和奥氏体不锈钢耐磨性的影响。
Effect of impact on wear resistance of high chromium cast iron and austenitic stainless steel has been studied by ball-on-ball impact and pin-on-disc abrasion test.