含碳量少于共析体(低于0.77%)的钢称为亚共析钢。
Steels having less than the eutectoid amount of carbon (less than 0.77%) are known as hypo-eutectoid steels.
含碳量少于共析体(低于0.77%)的钢称为亚共析钢。
Steels shaving less than the eutectoid amount of carbon (less than 0.77%) are known as hypo-eutectoid steels.
高于此点,由于超过共析点钢完全由珠光体和退火状态的渗碳体组成,硬度增加并不多。
Above this point the hardness can be increased only slightly, because steels above the eutectoid point are made up entirely of pearlite and cementite in the annealed state.
研究贝氏体相变的特点,弄清贝氏体相变反应与共析分解的区别极为重要。
It is important to understand the difference of bainite transformation and eutectoid decomposition in steels.
作为结果的组织结构是初步的共析铁素体(在共析反应前的铁素体)和部分珠光体的混合物。
The resulting structure is a mixture of primary or pro-eutectoid ferrite (ferrite that formed above the eutectoid reaction) and regions of pearlite.
熔敷金属组织主要是针状铁素体,少量的先共析铁素体。
Microstructure of the deposited metals is composed of acicular ferrite and a little proeutectoid ferrite.
熔敷金属组织主要是针状铁素体,少量的先共析铁素体。
The microstructure is composed of acicular ferrite and a little proeutectoid ferrite.
共析分解是个自组织过程,具有铁素体和渗碳体互为领先相的整合机制。
The eutectoid decomposition is a self organization process, which is characterized by the integrated mechanism that ferrite and cementite acted as prevenient phase alternatively.
为了准确地检验高碳过共析钢盘条中的网状渗碳体,分别对选用硝酸酒精溶液侵蚀和碱性苦味酸钠水溶液热侵蚀两种显示方法进行了比较。
In order to detect the carbide network in high carbon hypereutectoid steel wire rods accurately, two kinds of detection method of the carbide network are compared.
由于超过共析点钢完全由珠光体和退火状态的渗碳体组成,因此高于此点硬度增加并不多。
Above this point the hardness can be increased only slightly, because steels above the eutectoid point are made up entirely of pearlite and cementite in the annealed state.
高碳钢中加入的铬元素抑制先共析铁素体析出,减小珠光体片层间距,可明显提高抗拉强度,提高断面收缩率,改善线材的拉拔性能。
By cr microalloying, the fore eutectoid ferrite eduction is restrained, the distance between rows of pearlite is decreased, then the tensile strength, section shrinkage and drawing property of high...
结果表明,随冷却速率的增大,先共析铁素体的晶粒尺寸减小,体积分数增大,针状铁素体增多;
The results show that with the increase of cooling rate, the grain size of proeutectoid ferrite decreases, the volume fraction of proeutectoid ferrite and acicular ferrite increases.
结果表明,对于亚共析钢,在中温区变形、保温后可使先共析铁素体和珠光体组织大大细化,显著改善钢中铁素体和珠光体的分布状况;
The results show that, in hypoeutectoid steels, deformation at medium temperature may fine the structure and improve the distribution of ferrite and pearlite greatly;
当这种钢冷却时,就像图2.1的z - z线所示,除了初步的或预共析状态用渗碳体取代铁素体外,其余类似亚共析钢的情况。
When such steel cools, as shown in zz 'of Fig. 2.1 the process is similar to the hypo-eutectoid case, except that the primary or pro-eutectoid phase is now cementite instead of ferrite.
在较大焊接热输入条件下焊接,焊缝金属产生粗大先共析铁素体、过热区产生粗大粒状贝氏体,焊接接头低温冲击韧性因此降低。
The coarse primary ferrite appeared in weld metal, and coarse bainite appeared in heat-affected zone under larger heat input welding condition, which caused low...
在较大焊接热输入条件下焊接,焊缝金属产生粗大先共析铁素体、过热区产生粗大粒状贝氏体,焊接接头低温冲击韧性因此降低。
The coarse primary ferrite appeared in weld metal, and coarse bainite appeared in heat-affected zone under larger heat input welding condition, which caused low...