介绍了钛酸酯偶联剂表面处理碳酸钙的原理和方法。
The principle and method for surface modification of calcium carbonate with titanate coupling agent is described.
应用试验表明，绢云母经超细磨矿和偶联剂表面处理后，作为橡胶填料，填充性能得到明显的改善。
The results indicate that the filling properties in rubber of modified sericite powders were greatly improved, which had been confirmed by the application experiment.
采用硅烷偶联剂对无机填料和石棉纤维进行表面处理，提高无机填料与聚合物基体的界面相互作用；
The results show that after being treated with coupling agent, interface interaction between inorganic fillers or asbestos fiber and epoxy resin enhances quite a little.
所选用的不同种类的不同处理量的偶联剂对无机抗菌粉体的表面改性均有一定效果。
Then, some exciting results were found as follow: Inorganic antibacterial powder, modified with different coupling agents, showed different effects on its dispersion.
用硅烷偶联剂将几种常用的无机粒子进行表面处理后与ABS进行共混。
The surface property of inorganic particles is modified by the coupling agent before they are added into the ABS resin.
以甲苯二异氰酸酯（TDI）为偶联剂将正辛醇接枝到杉木粉表面，同时考察处理前后杉木粉填充PP复合材料的力学性能。
Octanol was grafted onto fir powder using TDI as coupling agent, then its application in PP composite materials was investigated.
本文应用单丝接触角测定仪测定了不同偶联剂处理的玻璃纤维临界表面张力。
Monofilament contact Angle meter has been used to measure the critical surface tension of glass fiber treated by different coupling agents.
研究工作中采用钛酸酯、铝酸酯、硼酸酯及硅烷偶联剂等表面改性处理剂，对滑石粉等填料进行表面改性处理，证明不同种类偶联剂存在一个最佳用量范围。
The surface modification of talc etc is treated by titanate, aluminate, borate and silane coupling agents, which testifies that content of different coupling agent exists an optimal range.
晶须表面用偶联剂处理。
采用含氟防水剂和硅烷偶联剂对剑麻纤维进行表面处理。
The surface of sisal fibers were treated by water proof compound a nd KH-550.
采用D L- 411 -A型偶联剂对高岭土进行表面活化处理，研制出相应的AK - 1型表面偶联活化改性高岭土。
After the surface of kaolin was modified by DL-411-A coupling agent, AK-1 active kaolin was acquired.
采用D L- 411 -A型偶联剂对高岭土进行表面活化处理，研制出相应的AK - 1型表面偶联活化改性高岭土。
After the surface of kaolin was modified by DL-411-A coupling agent, AK-1 active kaolin was acquired.
应用推荐