本文研究了氯乙烯—醋酸乙烯—丙烯酸酯三元悬浮共聚合反应中分散剂体系对树脂颗粒形态及溶解性能的影响。
The effect of dispersant systems in Vinyl Chloride-Vinyl acetateAcrylate suspension copolymerization on the resin particle shape and solubility have been studied.
实验结果表明:可使用硬脂酸锌作为分散剂,与其他物质配合,保证一定的量,将纳米氧化锌直接添加进低密度聚乙烯中可使复合材料表现良好的综合性能。
The experimental results proved that the direct addition of nano-ZnO to LDPE facilitated good combined properties for the composites by using StZn as the dispersing agent and other suitable materials.
研究了新型阻垢分散剂磺化苯乙烯共聚物ts—616的产品性能,与目前国外著名阻垢分散剂性能进行了比较。
The performance of a new scale dispersing inhibitor-sulfonated styrene copolymer ts-616 was studied and compared with that of famous foreign scale dispersing inhibitors.
采用不同体系分散剂、不同调粒剂用量合成了系列聚氯乙烯掺混树脂。
A series of Polyvinyl Chloride (PVC) blending resin were synthesized with different dispersion, additive content.
本文以苯乙烯和丙烯酸酯的低分子共聚物为B段,以含有极性基团的单体为A段合成了A—B嵌段型颜料分散剂。
An A-B blocked pigment-dispersing agent has been synthesised , in which the A block is a monomer with polar groups and the B fo'oek is the oligomer of styrene and acrylate with lower molecular weight.
通过大量试验分析了HPMC-E50和HPMC-F50在氯乙烯悬浮聚合中对PVC树脂的影响,从而确定了复合分散体系的质量分数以及分散剂的配比。
The effect of HPMC-E50 and HPMC-F50 on PVC resins in VCM suspension polymerization was analyzed based on a lot of experiments.
因此探讨了上述分散剂对悬浮法聚氯乙烯树脂颗粒特性的影响。
Thus discusses the effect of the dispersant on particle characteristics of PVC...
研究了聚合温度、反应时间以及引发剂、分散剂用量和交联剂形式及用量对树脂形态、凝胶分率和吸三氯乙烯、苯等的影响。
The effects of reaction temperature and time on the process were studied. The quantity of initiator, suspension agent, chemical and physical crosslinking agents on the resin's formation and...
研究了聚合温度、反应时间以及引发剂、分散剂用量和交联剂形式及用量对树脂形态、凝胶分率和吸三氯乙烯、苯等的影响。
The effects of reaction temperature and time on the process were studied. The quantity of initiator, suspension agent, chemical and physical crosslinking agents on the resin's formation and...