结果表明，造成主蒸汽滤网开裂的主要原因是晶界高温氧化，断口呈典型的沿晶开裂特征。
The results show that the main reason for the cracking was high temperature intergranular oxidation, with the fracture morphology being a typical intergranular cracking character.
结果表明，造成主蒸汽滤网开裂的主要原因是晶界高温氧化，断口呈典型的沿晶开裂特征。
The results show that the main reason for the cracking was high temperature intergranular oxidation, with the fracture morphology being a typical intergranular cracking character.