结果表明中间退火可以延长疲劳寿命。
The experiments showed that the intermediate annealing can prolong the fatigue life.
而最佳中间退火温度受合金成分的影响。
The optimum middle annealing temperature depends on the chemical composition of the alloys.
减少了中间退火工序,生产效率大大提高。
The interstage annealing procedure was reduced and the production efficiency wa...
合金的最佳中间退火温度随碳含量的增加而升高。
The optimal middle annealing temperature increases with the increase of the carbon content.
讨论了中间退火对轧制时立方取向稳定性的作用。
The effect of intermediate annealing is discussed in terms of the stability of cube orientation during rolling.
中间退火后晶粒细小,脱碳退火后晶粒细小均匀。
Grain size is small after intermediate annealing. Small and homogeneous grains are obtained after decarburizing annealing.
本文在实验的基础上提出的适合中间退火的工艺可稳定钼丝加工性能。
Base on experiment, this article presented some optimum technological parameters of middle annealing that can stabilize the processing properties of molybdenum wire.
采用晶体取向分布函数(ODF)研究和分析了中间退火对高纯铝箔立方织构的影响。
The effect of middle annealing on cube texture of high-purity aluminum foils was investigated by means of orientation distribution functions (ODFs).
中间退火工艺能改变电缆箔强度指标,提高其延伸率,减小各向异性,有利于铝箔的复合。
The middle annealing process can change the strength of cable foil, improve its elongation, reduce its anisotropy, and it's advantageous to the compound of aluminium foil.
重点研究了铝的纯度、均匀化制度、热轧温度、冷轧及中间退火对最终退火后箔材形成立方织构的影响。
The emphasis is put on effect of purity homogenization, hot rolling temperature, cold rolling and medium annealing on cubic texture of finally annealed foil.
采用热轧后温轧或中间退火后冷轧,再在一定温度下进行稳定化退火的工艺,可以获得综合性能良好的铝-镁-钪合金冷轧板材。
By warm rolling after hot rolling or cold rolling after annealing in process and stabilizing annealing in some temperature condition, the c.
没有中间温度预退火过程的薄膜,显示出(100)择优取向;
PLZT thin film without intermediate pre-annealing process displays (100)-preferential orientation.
结果发现,中间温度预退火过程可以影响薄膜对晶型结构的选择。
The results show that the intermediate pre-annealing process can affect the selection of crystalline texture.
要包括中间的软化退火和精加后的淬火及回火。
To include the quenching and tempering intermediate softening annealing and finishing after.
实践证明,采用高温淬火和中间消应力退火可显著提高其使用寿命。
Experimental results showed that the service life of die can be improved evidently by using high temperature quenching and stress relief annealing.
中间酸洗和氧化退火能较大幅度地降低氧化膜中碳的含量。
The extruding lubricant has the main effect on the carbon content.
中间酸洗和氧化退火能较大幅度地降低氧化膜中碳的含量。
The extruding lubricant has the main effect on the carbon content.