介绍了有机涂层中性盐雾试验的相关标准及其评价方法。
The standards and the comment process of neutral salt-fog test for organic coatings are introduced.
结果与失重法和中性盐雾试验法相比，有较好的一致性。
Its results have better consistency than those obtained by methods of weight loss and neutral salt spray.
涂层的耐蚀性采用中性盐雾试验和5%盐水浸润试验，并测试涂层的阳极极化曲线综合进行比较。
The corrosion resistance of the coating was measured by neutral mist of salt experiment and soaking in 5%nacl solution. Moreover, the curves of positive polarization were give...
采用中性盐雾试验测定了镀层的耐蚀性，采用内孔法测定了镀液的覆盖能力，并测定了镀层的硬度。
The corrosion resistance of deposits and covering power of the plating bath were tested respectively by neutral salt spray test and inner-pole method, and the hardness of deposits was also measured.
通过对中性盐雾试验中漆膜划痕处起泡现象的研究，分析了起泡产生的原因，提出了相应的解决方案。
Based on the study of the bubbling phenomena around the crosscut of coatings film in neutral salt spray test, this article has analyzed the cause of bubbling and proposes effective solutions.
探讨了彩涂板中性盐雾试验条件、试验注意事项、试验结果的评判，简要分析了影响试验结果的因素。
Test conditions, precautions in the test, evaluation of test results and factors affecting test results are analyzed in the article.
所获得的黑色钝化膜外观均匀，镀层钝化后经中性盐雾试验(连续喷雾)出现红锈(基体腐蚀)的时间大于1000小时。
The black inactivating film is homogeneous, and the inactivated coating, test shows, has a no red rust period longer than 1000 hr in neutral salt fog.
以45钢、A3钢、炮钢、20钢为金属试样，研究它们在中性盐雾加速试验及石家庄大气环境暴露试验中腐蚀失重与时间的变化规律。
The correlativity between neutral salt spray accelerated test and atmospheric corrosion test in Shijiazhuang was studied by the mass loss determination of 45 steel, A3 steel, 20 steel and gun steel.
用中性盐雾腐蚀试验来评价复合材料的耐蚀性，并用XRD检测了腐蚀产物。
Finally, the corrosion resistance of samples is evaluated by neuter salt-spray tests and corrosion products are confirmed by XRD.
中性盐雾、电化学测试等腐蚀性能试验结果表明，钛盐钝化溶液所获得的蓝色钝化膜，其耐腐蚀性能更优于铬酸盐钝化膜。
Corrosion resistance of the blue passivation film obtained in titanium salt solution was superior to that of the chromate passivation.
中性盐雾、电化学测试等腐蚀性能试验结果表明，钛盐钝化溶液所获得的蓝色钝化膜，其耐腐蚀性能更优于铬酸盐钝化膜。
Corrosion resistance of the blue passivation film obtained in titanium salt solution was superior to that of the chromate passivation.