本文研究了聚丙烯酸丁酯／聚甲基丙烯酸乙酯核／壳结构弹性体粒子对HIPS的增韧作用，提出了一个新的增韧机理。
The toughening of HIPS is studied by blending it with a polybutylacrylate/polyethylmethacrylate core/shell structure elastomer particles, an a new mechanism of toughening isproposed.
以醋酸乙烯酯和丙烯酸丁酯为主要原料，引入自交联型单体羟甲基丙烯酸胺合成了纸张——铝箔复合膜粘合剂。
The self - cross linking adhesive for paper - Al foil composite can be abtained by using vinyl acetate and acrylate as raw materials and hydroxy methyl acrylamide as self - cross linking monomer.
研究了聚甲基丙烯酸甲酯大单体与丙烯酸丁酯在苯中的共聚。
The poly macromer was copolymerized with butyl acrylate in benzene to form the graft copolymer.
乙酸丁酯稀释丙烯酸树脂后，用气相色谱法使丙烯酸树脂中的各种残余单体得到较好分离，再采用氢火焰离子化检测器(FID)定量测定。
Acrylic resin is diluted in ethyl acetate and the remnant monomer is well separated from it by gas chromatography and is quantificationally measured by hydrogen flame ionization detector (FID).
以甲基丙烯酸甲酯为硬单体，丙烯酸丁酯为软单体，丙烯酸为功能单体，环氧树脂为改性剂制备了密封胶用环氧改性丙烯酸树脂。
The epoxy modified acrylate resin for sealant is prepared with methyl acrylate as hard monomer, butyl acrylate as soft monomers, acrylate acid as functional monomers and epoxy resin as modifier.
探讨在采用瞬时聚合法直接合成固体丙烯酸酯浆料的过程中，疏水性单体丙烯酸丁酯用量对所生成丙烯酸酯浆料性能的影响。
Effect of hydrophobic monomer butyl acrylate amount on acrylate size mixture property in the process of compounding solid acrylate size mixture directly by instant polymerization was discussed.
采用酯交换工艺，在均相条件下，由甲基丙烯酸甲酯和正丁醇合成了甲基丙烯酸丁酯(BMA)。
Butyl methacrylate (BMA) was synthesized from n? Butanol and methyl methacrylate at homogeneous reaction by transesterification process.
本实验以甲基丙烯酸甲酯、丙烯酸丁酯和丙烯酸为主要原料，利用乳液聚合方法，制备了一种涂料用的纯丙乳胶。
A per-propyl emulsion for coatings, by emulsion polymerization, was prepared from methyl methacrylate (MMA), butyl acrylate and acrylic as raw materials.
研究了在间歇搅拌釜中以固体超强酸为催化剂，由丙烯酸和丁醇合成丙烯酸丁酯。
Catalytic esterification of acrylic acid and butyl alcohol for the production of butyl acrylate in batch stirred tank by using solid superacid was presented.
以丙烯酸、 丙烯酸丁酯和甲基丙烯酸甲酯为单体，采用自由基聚合法制备了聚丙烯酸卷材涂料前驱成膜物，获得了适宜的制备工艺条件。
Phragmoplast of coil coating has been prepared by free radical polymerization and by using acrylic acid, methyl methacrylate, butyl acrylate as the raw materials.
采用核壳乳液聚合方法合成了以甲基丙烯酸甲酯、 甲基丙烯酸和丙烯酸丁酯三元共聚物酸为核，聚苯胺为壳的导电高分子复合物。
Using emulsion polymerization, a conductive polymer composite was synthesized with polyaniline as shell , the polymer acid obtained by MMA MAA and BA as core.
由分析结果绘出了树脂相中的丙烯酸丁酯含量对蒸出溶剂相中的丙烯酸丁酯含量的回归线，建立了回归方程，并通过方差分析证实该回归方程是有意义的。
The ba level in resin vs ba level in vaporized solvent was plotted based on the results and a regression equation was established, which proves significant through variance analysis.
介绍了以丙烯酸、丙烯酸十二酯、甲基丙烯酸甲酯和丙烯酸丁酯为单体，采用反应型乳化剂，经过乳液聚合，制得了一种水性涂料用缔合型增稠剂。
A kind of associative thickener for waterborne coating is prepared by emulsion polymerization of acrylic, lauryl acrylate, methyl methacylate and butyl acrylate as monomers and reactive emulsifier.
介绍了以丙烯酸、丙烯酸十二酯、甲基丙烯酸甲酯和丙烯酸丁酯为单体，采用反应型乳化剂，经过乳液聚合，制得了一种水性涂料用缔合型增稠剂。
A kind of associative thickener for waterborne coating is prepared by emulsion polymerization of acrylic, lauryl acrylate, methyl methacylate and butyl acrylate as monomers and reactive emulsifier.