化学性能测试:材料的盐雾试验、不锈钢腐蚀试验等。
Chemical property testing: salt spray test of materials, corrosion test of stainless steel.
对发生泄漏的不锈钢u型波纹管补偿器的宏观失效特征、微观失效特征、金相、腐蚀介质进行试验分析。
A test analysis is made on macro-failure and micro-failure characteristics, metallography and corrosion mediums of U-type stainless steel bellows type expansion joints leaked.
通过高温抗氧化、盐雾腐蚀和应力腐蚀试验研究了07X16H6沉淀硬化不锈钢在使用状态(回火态)时的耐蚀性能。
The corrosion resistance of 07X16H6 precipitation hardening stainless steel in tempered state was studied using high temperature oxidation, salt-spray test and stress corrosion test.
采用浸泡、电化学、模拟试验以及拉伸试验对冷轧厂电镀锌机组不锈钢紧固螺栓在现行工艺条件下遭受严重腐蚀进行了研究。
The severe corrosion of stainless steel fastening bolts on Electrolytic Galvanizing Line(EGL)in cold strip mill plant under current working conditions has been studied.
本文通过一系列试验,建议现行的奥氏体不锈钢晶间腐蚀试验标准中的弯曲评定参数进行适当的修改,以有利于工厂生产和检验。
This paper proposed a suggestion for modification bend coefficient in the present standard. It would be beneficial to process of making stainless steel pressure vessels.
研究了该合金在长期储放热过程中对容器材料的腐蚀。腐蚀试验选用的容器材料是不锈钢(SS304L)和碳钢(C20)。
The corrosion resistance of some structural materials, including stainless steel SS304L and carbon steel C20, for the container of the alloy over a long heat storage or release period was studied.
金属腐蚀性试验结果对不锈钢,铜无腐蚀,对碳钢、铝基本无腐蚀性。
There are no erosion to stainless steel and copper and little erosion to coal, steel and aluminum.
通过金相观察、力学性能和耐晶间腐蚀性能试验,研究了SUS 304不锈钢M AG焊接头组织与性能。
The microstructure and properties of steel SUS304 MAG welded joint was studied through metallograph observation and property tests.
通过浸泡试验和金相显微镜研究了304不锈钢在腐蚀过程中马氏体含量的变化。
The change of martensite content of AISI304 stainless steels in corrosion solution was also studied by means of immersion test and metalloscope.
采用化学和电化学加速腐蚀试验方法对6种不锈钢的耐点蚀和缝隙腐蚀性能进行了评价。
Using accelerated chemical and electrochemical corrosion testing methods, the resistance to pitting and crevice corrosion behavior for six stainless steels were evaluated.
采用化学和电化学加速腐蚀试验方法对6种不锈钢的耐点蚀和缝隙腐蚀性能进行了评价。
Using accelerated chemical and electrochemical corrosion testing methods, the resistance to pitting and crevice corrosion behavior for six stainless steels were evaluated.