间苯二酚甲醛气凝胶是在一种类似生产白炭黑。
Resorcinol-formaldehyde aerogel is made in a way similar to production of silica aerogel.
利用超声波乳化技术,结合溶胶-凝胶反应制备了间苯二酚-甲醛有机气凝胶粉末和碳化气凝胶粉末。
Organic powder and carbon aerogel powder were prepared by sol-gel method with the help of ultrasonic emulsification technology using resorcinol and formaldehyde.
用8羟基喹啉、甲醛、间苯二酚及苯磺酸钠作原料合成了一种螯合树脂。
Formaldehyde 8 hydroxyquinoline sodium benzene sulfonate resorcinol copolymer described as chelating ion exchange resin was synthesized.
锦纶66帘子布浸胶液含有大量的天然胶乳、间苯二酚、甲醛、氨、乙烯、丁苯等有毒有害物质,其生产废水中COD和浊度特别高。
The dipping solution (DS) of nylon-66 cord fabric contains latex, resorcinol, formaldehyde, ammonia, ethene and butyl benzene. The COD content and turbidity in DS wastewater are very high.
实验需要的间苯二酚-甲醛(RF)气凝胶的孔径大于标准RF气凝胶所形成的孔径。
The pore size of resorcinol formaldehyde aerogels (RF) in experiments is bigger than that of standard RF aerogels.
试验研究改性间苯二酚-甲醛树脂GLR-20在半钢子午线轮胎胎体帘布胶中的应用效果。
The application of a modified resorcinol-formaldehyde resin GLR-20 in the carcass ply compound of PCR tire was experimentally investigated.
试验研究改性间苯二酚-甲醛树脂GLR-20替代间苯二酚对NR胶料性能的影响,并与进口产品B-20-S进行对比。
The effect of the modified phenolic resin GLR-20 replacing resorcinol on the properties of NR compound was investigated by using imported B-20-S as control.
以间苯二酚和甲醛为原料,采用溶胶-凝胶工艺,结合高温碳化和溶剂替换常压干燥技术,制备了碳气凝胶。
Carbon aerogels were prepared from resorcinol and formaldehyde via sol-gel process, high temperature carbonization and atmospheric pressure drying technology with solvent replacement.
以间苯二酚和甲醛为原料,采用溶胶-凝胶工艺,结合高温碳化和溶剂替换常压干燥技术,制备了碳气凝胶。
Carbon aerogels were prepared from resorcinol and formaldehyde via sol-gel process, high temperature carbonization and atmospheric pressure drying technology with solvent replacement.