结果表明，高铜镀层钢丝帘线与橡胶的初始粘合性能较好，但其老化后粘合性能下降明显；
The results showed that the steel cord with high copper content possessed better initial adhesion property to rubber, but the adhesion property after aging decreased significantly;
产品包装件捆扎整齐、钢丝镀层或包塑产品颜色均匀、一致。无漏镀、无破损。
3 product packaging pieces neatly, steel wire coating or plastic product color uniform, uniform. No leakage, no damage.
介绍密闭管道式钢丝热镀锌工艺、设备及技术参数，详细分析镀层的性能和工艺装置。
To introduce process, equipment and technology parameters of sealed pipe type hot galvanizing for steel wire and to analyze in detail property of coat and process devices.
由机械将双线绞合编织成多绞状、六边形网目的网片，其双线绞合部分的长度应不小于5cm，以不破坏钢丝的防护镀层。
The machinery will be woven into double stranded twisted hexagonal shape, multi mesh mesh, the double stranded part length should be less than 5cm, the protective coating without damaging the wire.
结果表明，钢丝热浸镀时走速过快和镀层不均匀是导致扭转脆性断裂的主要原因。
And quick wire movement during hot-dipping and inhomogeneous coating was identified as the main cause.
镀锌钢丝的耐蚀能力随镀层厚度增加而增加，随合金层厚度的增加而降低。
Anticorrosion property of galvanized steel wire can be improved by increasing Zn-coat thickness and be reduced by decreasing alloy layer thickness.
研究低铜镀层2+70.25HT钢丝帘线在轻型载重子午线轮胎带束层中的应用。
The application of low brass-plated 2+70.25HT steel cord in belt of LTR tire was investigated.
研究低铜镀层2+70.25HT钢丝帘线在轻型载重子午线轮胎带束层中的应用。
The application of low brass-plated 2+70.25HT steel cord in belt of LTR tire was investigated.