本文利用改进了的三甲基硅烷化方法研究低熟料沸石钢渣水泥。
An improved TMS method is used to study zeolite Ld-steel slag cement.
普通钢渣经处理可作冶金原料、水泥、路基材料等建筑用料和磷肥。
Usually steel slag is used as metallurgical materials, cement, roadbed materials, construction materials and phosphate fertilizer.
实验对比表明：与强度等级为32 . 5的纯水泥钢渣混凝土对比，掺入钢渣粉的砼强度略有降低，但能改善混凝土的和易性。
By test analysis compared with strength degree 32.5 of cement, strength of steel slag concrete is slightly decreased, but its fluidity is improved.
在高掺量矿渣水泥中掺少量可看作低质熟料的钢渣，弥补由于熟料掺量少造成的碱性不足。
Small amount of steel slag was used as low quality clinker in high addition of slag cement to compensate the lack of alkalinity caused by low clinker addition.
细述了钢渣的理化特性，并介绍钢渣在筑路、烧结矿、水泥、建材和农业等领域的综合利用。
The comprehensive utilization of steelmaking slag in all the fields was introduced such as road construction, sinter, cement, building material and agriculture.
研究了硅酸盐水泥添加钢渣膨胀剂后的物理化学性能和膨胀性能。
Chemical and physical properties and expansive property have been studied for steel slag expansive cement.
针对含有钢渣的植物纤维增强水泥基复合材料，研究了其基体结构和界面状况对材料性能的影响。
The effects of matrix structure and interface situation on properties of plant fiber cement-based composite materials with steel slag were studied.
通过正交试验进行了利用钢渣配制复合硅酸盐水泥的初步研究。
By orthogonal test, the research on preparing a composite Portland cement using steel slag was processed in this study.
介绍了水泥稳定钢渣路面基层施工过程中的质量控制方法及达到的效果。
The paper introduces the quality control methods and results achieved in construction of cement-stabilized steel slag pavement base.
试验研究了掺加磨细钢渣、粉煤灰等掺合料后水泥浆体导电性能的变化。
The effect of mineral blenders includes ground steel slag and fly ash on the electrical conductivity of cement mortar was studied.
本文试验用10% - 20%的水泥熟料及大量的以矿渣和钢渣为主的工业废渣，配置出325、425号绿色复合水泥。
In the paper, 10%-20% clinker and lots of waste slag, such as slag, steel slag, were used to prepared green cementing materials with the grade of cement 325 or 425.
本文介绍利用工业废渣—钢渣生产钢渣矿渣水泥，着重介绍钢渣矿渣水泥的生产工艺和应用。
The paper deals with production of cement from blast-furnace slag and steel-smelting furnace slag, especially with manufacture process and use of the cement.
由于钢渣成份波动大、易磨性差以及稳定性不好，钢渣用作水泥混合材或混凝土掺合料均难以达到高效、高值化利用的目的。
Steel slag is not better to produce cement or mineral admixture of concrete because of poor grindability, larger fluctuation of chemical and mineral components, poor stability and so on.
试验研究了在硅酸盐水泥体系中通过碱性激发提高钢渣水化活性的方法。
The Portland cement was used as an activator to improve the hydration activity of steel slag.
研究了由粉煤灰、矿渣、钢渣与一定量熟料组成的粉煤灰矿渣复合水泥中各组分对水泥的强度协同效应以及影响协同效应的主要因素。
The strength synergistic effect of each component on composite Portland cement with fly ash, slag, steel slag and a certain amount of clinker and its influence factors are studied.
本文针对转炉钢渣能否作为混合材的课题对宝钢转炉钢渣进行了一些理化研究，并且探讨与其它混合材一起掺入水泥中生产混合水泥的可能性。
Theoretical studies are carried out on the slag of tilting converters in Baoshan Steel Works as an cement addition and the possibilities to make blended cement with other additions.
分形维数与钢渣微粉的比表面积间满足良好的线性关系，并与钢渣基水泥材料的胶凝性能良性相关。
A good linear relationship meet between fractal dimension and specific surface area of slag powder, and positive correlation with the cementitious properties of steel slag-based cement material.
本文在实验室研究的基础上，采用钢渣掺量为60%的复合微粉替代50%的水泥，配制C30混凝土，进行了工业应用试验。
According to the laboratory studies, C30 concrete was prepared dosed micro-powder mixture with 60% steel slag to substitute for 50% cement and the concrete was used in industrial application test.
水泥抗压强度随钢渣掺量的增加而有所降低，水泥安定性合格。
The compressive strength of cement is somewhat reduced with the increase of the slag quantity mixed, however, the soundness remains qualified.
钢渣粉煤灰路面基层材料的长期强度介于水泥稳定碎石和二灰稳定碎石之间，可用于各等级公路基层底基层的修筑。
The long term strength of it is between the cement stabilized broken stone and lime fly ash stabilized broken stone. It can be used as road base and subbase material in any degrade highway.
研究了转炉钢渣粉对矿渣粉-硅酸盐水泥混合胶砂硬化体收缩特性的影响。
The effect of converter steel slag powder(CSSP), on the shrinkage characteristic of hardened GGBFS-PC mixed mortar is studied.
对于后期强度，水泥含量虽影响最大，但钢渣细度和陈化龄期的影响明显增强。
But the factor of the steel slag fine and aging times have relatively more and more significant influence on the later compressive strength and the cement content is still the most influential factor.
研究表明，钢渣掺入量<30%时，硅酸盐水泥对钢渣的活性激发效果最好；
The research indicated that, the Portland cement had a best effect to enhance the activity of steel slag when the admixture amount of steel slag was less than 30%.
结果表明，钢渣掺入水泥中可以改善水泥浆体的流动性。
Rusults show that mobility of cement paste can be improved when steel slag is added to cement.
主要研究单掺钢渣以及钢渣与矿渣复合后对水泥浆体各项物理力学性能的影响。
Steel slag and mixing with blast furnance slag influent on performances of cement paste was discussed.
结果表明：钢渣的掺入可以改善水泥浆体的流动性，凝结时间随钢渣掺量增加而延长。
The results show that mobility of cement paste was improved after adding steel slag and setting time extends with the addition of steel slag increasing.
本发明涉及一种水泥新品种，更确切地说涉及一种磷渣钢渣白水泥及其制备方法。
This invention USES phosphorus residue, steelmaking slag and calcined plaster as components of the clinker-free white cement.
本发明涉及一种水泥新品种，更确切地说涉及一种磷渣钢渣白水泥及其制备方法。
This invention USES phosphorus residue, steelmaking slag and calcined plaster as components of the clinker-free white cement.