沿着顺流方向冲蚀磨损率减小；
发现在一定滑动速度下磨损率有一峰值。
比磨损率也与温度、气氛和接触压力密切相关。
The specific wear rate is strongly dependent on the temperature, atmosphere and contact pressure.
可作为刀具瞬时磨损率神经网络测量的端系统。
It can be applied in neural network measurement for the instantaneous wear rate of cutting tools.
在试验范围内，电流比载荷对磨损率的影响显著。
Current has obviously affected on wear rate compared with loading.
氧气流量、燃气流量适中的条件下制备的涂层磨损率较低。
Moreover, the coatings with comparative lower abrasive wear rate can be deposited in the condition of moderate flows of oxygen and propane.
通过回归分析，建立了切削效率和刀具磨损率的数学模型；
The mathematic models of machining efficiency and wear of cutter were founded by analysis of regression about experimental results.
相比之下，怀疑金属过敏者且假瘤者，磨损率不变或者更低。
In contrast, among those with suspected metal hypersensitivity, wear rates were the same or lower in those who had pseudotumors.
弹性金属塑料材料的磨损率随滑动速度和载荷的升高而增加。
The wear rate of EMP increases with the increase of velocity and load at a different pace under various test conditions.
利用回归分析，建立了成型修整加工刀具磨损率的数学模型。
The mathematic model of wear of cutter about molding finishing machining was founded by analysis of regression.
股骨侧组件磨损率在表三中显示，髋臼侧磨损率显示在表4。
Median femoral component wear rates are shown in Table 3, acetabular component wear rates, in Table 4.
磨合试验中还发现了因齿面副两表面磨损率差形成的负电阻现象。
The negative oil film resistance is also found in the running-in, which results from the wear rate difference of the pair.
当其余各影响参数保持一定值时，磨损率随接触面积的增大而增大。
While giving other parameters, wear rate increases along with the increase of contact area.
以上处理的试样经磨损试验，得到了磨损率和机械性能的一些关系。
Wear and tear tests of the treated specimen are made by Brinell wear test machine, and the relation between wear rate and mechanical property is set up.
试验表明硬度与其磨损率呈非线性关系，磨损率是由多因素决定的。
The experimentation shows that hardness and wear show non linear relation. The rate of wear depends on many factors.
以上处理的试样经磨损试验，得到了磨损率和机械性能的一些关系。
Wear and tear tests of the treated specimen are made by Brinell wear test machine, and the relation between wea...
钢轨材料的磨损率随对应车轮硬度的增加而增加，且近似呈线性关系。
The wear rate of rail steel increases linearly with the hardness of the corresponding wheel steel rising.
结果表明：材料的磨损率随载荷的增加和磨损速度的增大而逐渐增大；
The results show that the wear rate increases with the increasing of load and wear speed;
研究了配副硬度差与磨损率的关系，根据这种关系确定了最佳配副组合。
By investigating the relations of hardness difference to wear rate, the best friction pair mate was ascertained.
EMP磨损率随滑动速度和载荷的升高耐增加，但不同试验条件的增幅不同；
The wear rate of EMP increased with increasing of velocity and load at different rates under various test conditions.
研究了铝合金及不同成分复合材料在不同温度及载荷下的摩擦系数和磨损率；
The friction coefficients and wear rates of the aluminum alloy and composites reinforced with ceramics of different volume fractions were measured at various temperatures and loads.
随着高温保温时间的延长，低碳高铬铸铁的磨损率降低幅度较大，耐磨性能提高。
With increasing of the holding time at high temperature, wear rate decreasing of low C-hi cr cast iron became more obvious, and wear resistance increased.
结果表明，在不同磨粒磨损条件下，马贝复相组织的磨损率具有相同的变化趋势。
The experimental results show that the rate of wear has the same varying tendency under different wear conditions.
表面粗糙度有一个最佳值，在这个表面粗糙度下电弧能量最小、质量磨损率也最小。
There is an optimum surface roughness which will produce minimal arc energy and minimal wear rate.
钢背-锡青铜双金属衬套制造成本低、磨损率小、使用寿命长，可取代全青铜衬套。
Steel backed-tin bronze bi-metallic sleeve can be used to substitute all bronze sleeves due to its low manufacturing cost, better wearing quality and longer service life.
低摩擦系数—切屑与刀具间的摩擦系数应当较低。这会使磨损率较小及切屑流动更好。
Low friction-the coefficient of friction between the chip and tool should be low. This would allow for lower wear rates and better chip flow.
研究了金属基体及其中镍铬合金的含量对复合材料的硬度、摩擦系数和磨损率的影响。
The effects of metal base content and NiCr alloy addition on hardness, friction coefficient and wear rate of the composites were studied.
用双隐层BP人工神经网络，建立了丝杆螺母副的磨损率与滑动速度关系的数学模型。
By the use of double hidden layered BP artificial neural network a mathematical model of relationship between wear rate of screw-nut pair and sliding speed is established.
随退火温度的升高镀层摩擦系数呈现出先降低后升高的变化趋势，比磨损率逐渐增大。
Although the specific wear rates of the coatings increase obviously as the annealed temperature increase, the coefficient of friction exhibits decrease first and then increase.
结果表明：磨损率随载荷和磨粒粒径的增大而增加，但磨损速度对磨损率的影响甚小。
The results indicate that the wear ratio increases with the increase of the wear load and grit size, but the wear rate has less effect.