对硼硫酸阳极氧化对铝合金疲劳性能的影响进行了测试。
The influence of BSAA on fatigue performance of aluminum alloy is tested.
表明BP ANN是硫酸阳极氧化制备多孔膜孔有序度的较好的预测模型。
The result shows that BPANN is a good model to predict the hole ordering for PAA film in sulphuric acid.
研究了铜与1-（2-吡啶偶氮）-2-萘酚（PAN）的显色反应，建立了测定硫酸阳极氧化液中铜的新方法。
The color reaction conditions of Cu 2+ and 1-(2-pyridylazo)-2-naphthol(PAN)were researched, and a new method was developed for the determination of copper in sulfuric acid anodizing liquor.
研究了硫酸阳极氧化和铬酸阳极氧化工艺对LY 12 CZ板材、LC9CS棒材在中值寿命区疲劳强度的影响。
This paper studies the effects of the sulfuric acid anodizing and chromic acid anodizing on the fatigue strength in the intermediate value life zone of LY12CZ plate and LC9CS bar.
本文系在硫酸、硫酸亚锡溶液中对添加有稀土的6063变形铝合金进行了阳极氧化和电解着色。
The anodic oxidation and electrolytic colouring of 6063 aluminum alloy containing rare earths in solutions of sulfuric acid and stannous sulfate are studied.
采用恒电压电解法研究了铝在硫酸中的阳极氧化过程。
The anodic oxidation process of aluminum in sulfuric acid was investigated using constant voltage electrolysis method.
而硫酸铅的阳极氧化反应则是众所周知的。
本文用椭园法、交流阻抗及电位测量研究了钛阳极氧化膜在0.5N硫酸中的溶解规律和耐蚀性。
Ellipsometry, A. C. impedance and potential measurements have been used to study the dissolution behaviour and corrosion resistance of titanium anodic oxide film in 0.5n sulfuric acid.
研究了一些常见的羧酸以及硫酸浓度等对铝合金中温阳极氧化膜的厚度和硬度的影响。
The effect of some common carboxylic acids as well as sulphuric acid concentration on thickness and hardness of medium temperature anodizing film of Al alloy was investigated.
采用自制脉冲恒流电源，研究了缝纫机零部件（2A12）在低硫酸浓度下的脉冲恒流硬质阳极氧化工艺。
The hardened anodic oxidation coating on sewing machine components(2A12)was investigated in different sulfuric acid density solutions with special apparatus.
对工业纯铝在硫酸溶液中采用硬质阳极氧化的方法制取氧化膜的工艺进行了研究，在传统硫酸硬质阳极氧化工艺的基础上进行了改进。
By hard anode oxidation, the film is obtained when industrial pure aluminum is in sulfuric acid solution, make the improvement in the traditional sulfuric acid hard anodizing craft foundation.
对铝在硫酸溶液中采用阳极氧化的方法制取厚氧化膜的工艺进行了研究。
By anode oxidation, thick film is obtained when aluminium is in sulphuric acid solution.
研究了一种采用双向脉冲电源将铝合金阳极氧化膜在硫酸铝溶液中进行封闭的绿色工艺。
A new pulse sealing treatment, involving the use of an asymmetric pulse power supply to seal the anodic film on an al substrate immersed in a solution of aluminum sulfate, has been developed.
本文探索了在草酸和硫酸电解液中，铝阳极氧化自组织形成有序纳米六方结构氧化铝的条件。
The conditions for self-organized formation of nano-sized and ordered hexagonal anodic alumina arrays were investigated for both solutions of oxalic acid and sulfuric acid as electrolyte.
研制了以硫酸、草酸、酒石酸为主要成分的铝合金硬质阳极氧化电解液。
An electrolyte solution with sulfuric acid, oxalic acid and tartaric acid as the main component for aluminium alloy hard anodization was developed.
本发明提供了一种在低温条件下，采用硫酸铵回收硬质阳极氧化过程中废硫酸的新方法。
The invention provides a novel method for recycling waste sulfuric acid in the oxidation process of hard anode using ammonium sulfate at low temperature.
在硫酸电解液中加入适量由羧酸和有机化合物组成的添加剂 ，制得铝合金阳极氧化膜。
Structure, composition and corrosion resistance of the anodic oxidation film on the magnesium alloy surface were discussed.
在硫酸电解液中加入适量由羧酸和有机化合物组成的添加剂 ，制得铝合金阳极氧化膜。
Structure, composition and corrosion resistance of the anodic oxidation film on the magnesium alloy surface were discussed.