探讨了热处理制度对高铬铸铁硬度的影响。
Effects of heat treatment schedule on the hardness of high chromium cast iron are discussed.
报导了通过改变热处理制度调整铝合金锻件强度与塑性指标。
This paper reports that the strength and Plasticity of aluminium alloy forging is adjusted by changing system of heat treatment.
研究了不同的热处理制度下该钢的显微组织、力学性能及磨损行为。
The microstructure, mechanical properties and tribological behaviors of the steel treated by different heat treatments were studied.
研究了不同热处理制度对一种新型的低层状析出气阀钢LF6性能的影响。
This paper presents the effect of different heat treatments on performance of new low layer separation valve steel LF6.
通过调整合金成份和改变热处理制度试验，有效地提高了低温钢的低温韧性。
The low temperature toughness of low temperature steel can be improved effectively by means of adjusting alloy ingredients and modifying heat-treatment regime.
在光学显微镜下考察了不同热处理制度下可加工微晶玻璃陶瓷的组织和结构。
Microstructure of machinable glass-ceramics prepared in different processes of heat treatment was investigated by optical microscope.
研究了合金化元素对新型高强韧炮钢的热处理制度、显微组织和力学性能的影响。
Effects of the alloying elements on the heat-treatment process, microstructure and mechanical properties of a novel gun steel combined with high strength and toughness were investigated.
比较分析了国内几种具有代表性的顶头材质，分析研究了有关的生产工艺及热处理制度。
The typical kinds of plug materials are compared and analyzed and the manufacturing processes and the heat treatment systems of the plugs are also studied.
考察热处理制度对抗菌块体的制备及结构、银价态、银离子释放速度、抗菌性能的影响。
Heat treatment on the preparation, structure, electrovalence of silver, releasing speed of Ag ions and antibacterial property of obtained blocks were investigated.
钢含磷量提高到0．9％以上，控制钢丝的热处理制度，使过共析钢丝强韧性显著提高。
The strength and tenacity of super-eutectoid steel wire have been improved notably by increasing the carbon content of the steel to more than 0.9% and controlling the heat-treatment system.
影响堆焊金属性能的主要因素是堆焊金属的成分、堆焊工艺参数及焊后的热处理制度等。
The composition of surfacing metal, flux, process variables and heat-treating condition are the main factors influencing the characteristics of surfacing layer.
当合金设计出来后，若加工工艺和热处理制度制定得不当，也会降低合金设计的预期值。
The expected effects of alloy design may be deteriorated after the alloy is designed if the established operational regime is less appropriate to process technology and heat treatment.
最后依据上述实验得出的最佳工艺参数范围及合适的热处理制度进行锻件工艺试制，确定主导工艺。
At last we can decide the leading technique by using the best scope of technique parameters and the suitable thermal treatment system gained by above experiment to test a forging technique.
通过多种热处理工艺研究，已发现几种热处理制度能使合金塑性提高，且具有优良的综合力学性能。
Through research on the heat treatment processes, we have found the proces-ses which enable the alloy to increase ductility and possess a good c…
将出无氧化加热段的带钢继续加热到热处理制度要求的温度，并在保护气氛中对带钢表面微弱的氧化膜起还原作用。
The strip is heated here to required temperature and the light oxide film on the strip is reduced by protection atmosphere.
本文运用金相组织分析的手段，对具有可比性的反弯试验的三种热处理制度下的样品进行分析，展示了金相组织与反弯性能之间的联系。
The article analyses the samples under the three heat treatment systems of inflection test with comparability, and illustrates the relation between metallographic structure and inflection performance.
讨论冶金品质、镁硅质量比、微量稀土及热处理制度对60 63铝合金导热性能的影响，在分析实验数据的基础上，阐述了各影响因素的作用机理。
The effects of four factors on heat exchange of 6063 aluminum alloy are discussed. With analysis of experimental data, action mechanism of each factor is expatiated.
本文为提高自行车钢圈用带钠的尺寸精度和各项性能进行了轧制和热处理工艺试验，得出了好的工艺制度。
In order to increase the dimensional accuracy and other properties of strip steel used for the tyre rim of bicycle, the experiments on rolling process and heat treatment are made.
文章研讨了高磁导率合金磁导率的影响因素，可采用合理的热处理工艺制度加以有效地控制，从而提高材料的磁性能。
Influence factor for the high-permeability alloy are studied in this paper. Employing reasonable control process for heat treatment technology, the magnetic properties of materials were improved.
利用光学显微镜和透射电子显微镜对不同热处理工艺制度下高性能耐火耐候建筑用钢的显微组织进行了观察和分析。
The microstructure of high performance fire-resistant and weathering construction steel after different heat treatment regimes was studied by using OM and TEM.
拟定了试验用焊丝盘条的化学成分、轧制制度，以及焊丝生产的热处理和拉拔制度。
To draft the chemical composition, rolling system of wire rods for welding wire for test, and the heat-treatment and drawing system for welding wire production.
结果表明阶梯制度的热处理方式适用于本体系的遮色瓷。
The results showed that the staircase heat treatment schedule was fit for preparing the opaque porcelain.
结果表明阶梯制度的热处理方式适用于本体系的遮色瓷。
The results showed that the staircase heat treatment schedule was fit for preparing the opaque porcelain.