阐述了超高强度的淬火回火钢（调制钢）在深海半潜式钻井平台中的应用。
This paper describes the application of high strength quenched and tempered steel in semi-submersible drilling platform.
钢的热处理操作主要有三种，即：淬火、回火和退火。
There are three main operations in the heat treatment of steel: hardening tempering and annealing.
钢的热处理操作主要有三种，即：淬火，回火和退火。
There are three main operations in the heat treatment of steel: hardening, tempering and annealing.
与经普通淬火和高温回火的相比，经磁场淬火和高温回火的T10钢的抗拉强度提高了28%，断后伸长率提高了8。
The tensile strength, elongation and hardness of T10 steel subjected to magnetic field quenching and to high temperature tempering were separately increased by 28%, by 8.
钢板应为全镇静钢且经奥氏体精细粒度处理。规格化的，规格化及回火的或淬火及回火。(译文请指正)。
The plates shall be fully killed and shall be fine austenitic grain treated. They shall be normalized, normalized and tempered or quenched and tempered.
本文介绍国产A508-3钢在不同的淬火、回火和退火条件下的热处理实验的某些结果。
This paper presents some results of heat treatment experiments of A508-3 steel at different quenching, tempering and annealing conditions.
试验结果表明H13钢在最佳完全退火温度、淬火温度、回火温度下可得到最优综合性能。
The test results show that the surface of H13 steel can obtain the optimum performance at temperature of complete annealing, quenching and tempering.
铬钒钢盘条金属丝和弹簧。高负荷地线。淬火和回火。规范。
Chromium - vanadium steel wire rod, wire and springs - high duty ground wire - hardened and tempered - specification.
研究了T10钢在低温盐浴渗铬后直接淬火并回火工艺。
Immediate quenching and tempering process of steel T10 after low temperature salt bath chromizing was studied.
关于钢的淬火和回火有两个要点需要注意。
Two important points are to be noted in connection with the quenching and tempering of steel.
同时，提出了一种确定淬火钢回火工艺的新方法。
And, a new method of determining the technology of tempering of the hardened steel is also advanced.
试验测定了该钢的CCT曲线，探讨了淬火和回火加热温度对该钢力学性能的影响。
Its CCT curve was determined by test. The influence of quenching and tempering temperature on the mechanical properties was also studied.
利用等温回火实验，采集了淬火钢在不同条件下回火时的硬度数据。
The hardness data of quenched steel under different conditions were collected utilizing austempering tests.
研究了回火温度对钢淬火后性能的影响。
The effects of tempering temperature on properties of quenched link-chain steel were studied.
研究了淬火、回火工艺对低碳马氏体型高强度高韧性非调质钢的组织和性能的影响。
The effect of hardening and tempering process on the organization and performance of high-strength and high-toughness non-hardened-and tempered steel of low carbon martensite is researched.
国产新型塑料模具钢主要有预硬钢、时效硬化钢、淬火——回火钢、冷挤压成型模具钢、耐蚀钢等类型。
The new domestic - developed plastic mould steels include prehardening steel . age hardening steel, quenching-tempering steel, cold -forming steel, and anti - corrosion steel, etc.
此外，磁场淬火还提高了T10钢的抗回火能力，这是由于磁场淬火后的钢中含有大量弥散碳化物所致。
In addition, the magnetic field quenching will increase the resistance of the T10 steel to tempering because of a large amount of dispersed carbides in the steel after magnetic field quenching.
介绍两种高铬马氏体不锈钢的油淬火回火工艺原理；
The principle for the oil-quenching and tempering technology of two high chromium martensitic stainless steels is introduced.
研究了H13钢的锻造、预备热处理、淬火回火、表面热处理对其性能和模具寿命的影响。
The effects on the properties and die lifespan of forging, conditioning heat treatment, quenching ami tempering, surface heat treatment are researched.
高张力钢60公斤类生产后的淬火科技回火热处理工艺。
High tension steel the 60kg class is produced after heat treatment process of quenching & tempering.
经淬火及回火后的合金层具有高速钢组织及性能。对渗金属层渗碳后的组织进行了电子显微分析。
The carburized alloyed layer possesses high density of finery and dispersed alloy carbides for the high concentrations of W, Mo and their affinities with carbon.
另外为消除二次淬火对ASTM 4130钢组织和性能的影响，应采用多层多道焊，并添加回火焊道。
In addition, to weaken the effect of double quenching on the microstructure and properties of ASTM4130 steel, multi-pass welding and temper bead should be adopted.
另外为消除二次淬火对ASTM 4130钢组织和性能的影响，应采用多层多道焊，并添加回火焊道。
In addition, to weaken the effect of double quenching on the microstructure and properties of ASTM4130 steel, multi-pass welding and temper bead should be adopted.