腐蚀介质和介质温度对沟槽腐蚀敏感性系数无显著的影响。
The corrosive solution and test temperature have no apparent effects on the grooving corrosion sensitivity coefficient.
而不连续流线组织的钢板具有较低的沟槽腐蚀敏感性，在焊缝处产生单腐蚀沟槽。
The steel with discontinuous flowline microstructure has lower grooving corrosion susceptibility and only single corrosion groove exists along the welding line.
作者从介质的组成、相组成、流动特性和材质等方面，对沟槽腐蚀的成因进行了讨论分析。
Cause of formation of groove corrosion was analyzed from various aspects such as composition of medium or phase, characterization of flow, quality of material and so on.
设计了利用KOH溶液定向腐蚀制作出的平行四边形蚀坑串，所形成的锯齿状沟槽结构来固定光纤。
The dentate groove is devised which is composed of a series of the etched parallelogram pits in KOH solution.
广泛使用于化工厂的储罐、管道、沟槽、杆、架等，污水处理的设备、混凝土池和槽，脱硫装置设备、排烟烟囱，作为耐强腐蚀介质的涂层。
Widely used on the storage tank, pipe, channel etc. Besides used on the equipment of the waster disposal plant, concrete pool, chimney as the anticorrosive coating.
推荐用途广泛使用于化工厂的储罐、管道、沟槽、杆、架等，污水处理的设备、混凝土池和槽，脱硫装置设备、排烟烟囱，作为耐强腐蚀介质的涂层。
Recommended Uses Widely used on the storage tank, pipe, channel etc. Besides used on the equipment of the waster disposal plant, concrete pool, chimney as the anticorrosive coating.
到目前为止，树脂混凝土已经在防腐蚀整体地面、设备沟槽等工程中得到广泛的使用。
Up to now, polymer concrete has been increasingly used in some engineering, such as anti-erosion monolithic floor and equipment groove.
综合分析了碳钢表面出现腐蚀沟槽的原因。
The reason for formation of corrosive ditch was therefore analyzed synthetically.
腐蚀后的上隔离沟槽边缘平整，其深度和宽度可以解决注入电流在相邻像素之间产生的干扰问题。
The edges of the grooves after etching are plane and smooth. The depth and width of the grooves can solve the interference problem induced by the injection current between the adjacent pixels.
腐蚀后的上隔离沟槽边缘平整，其深度和宽度可以解决注入电流在相邻像素之间产生的干扰问题。
The edges of the grooves after etching are plane and smooth. The depth and width of the grooves can solve the interference problem induced by the injection current between the adjacent pixels.
应用推荐