本发明涉及一种氯丁胶粘剂的制备方法。
The invention relates to a method for preparing a chloroprene rubber adhesive agent.
本发明提供一种氯丁胶乳胶粘剂及其制备方法。
The invention provides neoprene latex adhesive and a preparation method thereof.
研究了几种阻燃填料在氯丁胶乳涂料中的阻燃作用。
The fire retardant mechanism of a number of fire retardant fillers in neoprene latex coatings has been studied.
介绍了国内外氯丁胶粘剂、涂料领域的进展情况。
The development in research of adhesives and paints based on chloroprene rubber was reviewed with 36 references.
介绍了应用时氯丁胶乳砂浆的配比、施工程序和要点。
Mixing rate of polychloroprene latex slurry, construction procedures and its main points in the application are introduced.
讨论了原料配比、聚合工艺对接枝氯丁胶性能的影响。
Effect of raw material ratio and polymerizing process on the properties of the grafted chloroprene adhesive was discussed.
这种胶粘剂的性能均超过普通氯丁胶粘剂，生产成本低。
All of the performances of said adhesion agent surpass that of the ordinary neoprene adhesion agents but the productive cost is lower.
本文简述了一种用于喷涂的氯丁胶粘剂配方，制备工艺及性能。
The formulation, preparation technology and properties of neoprene adhesive for spraying are described in brief.
试验了不同盐酸含量的氯丁胶活性剂对丁基硫化胶质量的影响。
The effects of neoprene activator with varied HCl level on cured IIR compound performance have been tested.
介绍了氯丁胶乳改性阳离子乳化沥青的配方、工艺及其性能特点。
Formulation, process technology and properties of cationic chloroprene latex modified emulsified pitch paint for Bridges are introduced.
介绍了用酚渣油树脂替代酚醛树脂，制作氯丁胶胶浆粘合剂的研究。
This paper reports the research of preparing adhesive for chloroprene rubber glue by using phenolic residue resin as a substitute for the phenolic resin.
在生产油性氯丁胶涂料时，因温度高，易失火，给生产带来极大的危害。
When manufacturing oil neoprene paint, it is on fire easily due to high temperature, and brings huge harm to production.
其中的可接枝CR- 244将是氯丁胶粘剂行业很有潜力的新产品。
The grafting CR - 244 among it will be more potential new product in the polychloroprene adhesive trade.
氯丁胶粘剂的低毒混合溶剂的选择原则是：根据溶剂的氢键指数及溶解度参数。
The selection principal of low toxic mixed solvent of CR adhesive is depended upon hydrogen bond index and solubility parameter of the solvent.
橡胶内层的材质为天然胶或三元乙丙橡胶，外层橡胶的材质为氯丁胶或三元乙丙橡胶。
The rubber inner layer is made of natural gum or ethylene propylene diene rubber, and the rubber outer layer is made of chloroprene rubber or ethylene propylene diene rubber.
介绍了LB - 7氯丁胶乳水泥砂浆的组成、配方、性能，探讨了影响性能的因素及机理。
Composition, formulation, properties of LB-7 chloroprene latex cement mortar are described and factors influencing properties and mechanism are explored.
通过采用氯丁胶乳改性混凝土及环氧砂浆面层进行更新改造，投用两年多，至今没有任何损坏。
After the replacement with modified concrete of chloroprene latex and epoxy cement mortar, no damages have been found after two years of operation.
试验结果表明：树脂交联剂的羟甲基含量和氯丁胶中的盐酸含量对丁基硫化胶质量有很大的影响。
The results show that the hydroxymethyl content of resinous crosslinking agent and HCl content of neoprene activator will considerably effect on cured IIR compound performance.
研究表明，用酚渣油树脂取代酚醛树脂改性接枝氯丁胶是成功的，为酚渣油树脂的应用开辟了一个新途径。
It shows that to substitute phenol resin with phenolic residue resin is very successful and the coat of production is reduced. Thus a new aspect for phenolic residue resin is setup.
研究了影响氯丁胶粘剂拉伸强度主要因素，探讨了混炼胶、溶剂、树脂等对氯丁胶粘剂拉伸粘接强度的影响。
It is studied that the main influence factors on adhesive strength of CR adhesives, including mixed rubber, solvent, resin etc.
前言：研究了影响氯丁胶粘剂拉伸强度主要因素，探讨了混炼胶、溶剂、树脂等对氯丁胶粘剂拉伸粘接强度的影响。
It is studied that the main influence factors on adhesive strength of CR adhesives, including mixed rubber, solvent, resin etc.
不少单位解决老建筑渗漏的措施是应用沥青油毡、SBS改性沥青柔性油毡、氯丁胶等修补资料在渗漏处进行修补。
Many units solve the old construction leakage means are use patching materials and so on asphalt felt, SBS modifying asphalt flexible linoleum, neoprene to infiltrate the leak to carry on patching.
使用上述方法制成接枝氯丁胶粘剂中有害物质限量完全达到GB 19340- 2003《鞋和箱包用胶粘剂》国家标准。
The limit amount of the hurtful materials from the grafted chloroprene adhesive manufactured by the above method reached GB19340-2003 National Standard< …
根据尿素包装厂房出现的腐蚀现象和产生原因确定了整改思路，经过性能和价格比较，选用性价比高的氯丁胶乳砂浆对腐蚀的地面进行维修。
Concerning the corrosion of the urea workshop and its causes, and polychloroprene latex slurry is selected to repair the corrosive ground after the comparison of performance and prices.
纤维表面漫胶处理后断裂强力提高，当UHMWPE纤维中改性氯丁胶或聚氨酯粘结剂的含量为6%时，其断裂强力增加17.2%或13.9%。
When the modified neoprene or polyurethane adhesive content in UHMWPE fibers was 6%, the strength of UHMWPE fibers increased 17.2% or 13.9%, respectively.
纤维表面漫胶处理后断裂强力提高，当UHMWPE纤维中改性氯丁胶或聚氨酯粘结剂的含量为6%时，其断裂强力增加17.2%或13.9%。
When the modified neoprene or polyurethane adhesive content in UHMWPE fibers was 6%, the strength of UHMWPE fibers increased 17.2% or 13.9%, respectively.