介绍桐油改性线型酚醛树脂的制造方法及应用研究。
This article recommends manufacture and application of the novolacs resin modified by tung oil.
研究了硼桐油改性酚醛树脂的合成工艺，对其物化性能进行了试验研究和分析。
The synthesis process of phenolic resin modified with boron and tung oil is given in this paper, its physical and chemical properties are studied by test and the relative analysis is carried out.
结果表明，桐油改性酚醛树脂的剪切强度、冲击强度较未改性树脂大，硬度适中。
The results showed that the shear strength and impact strength were superior to those of pure resin, and the hardness was mezzo.
给出了硼-桐油改性酚醛树脂的合成工艺，并对其物理化学性能进行了试验研究和分析。
The synthesis process of phenolic resin modified with boron and tung oil was given, its physical and chemical properties were studied and analyzed.
以六甲氧基甲基三聚氰胺树脂（HMMM）为交联剂，制备桐油改性醇酸氨基水性绝缘漆。
With HMMM as cross-linked agent, waterborne alkyd-amino insulation paint modified by tung oil was prepared.
桐油改性水性醇酸树脂油度增大，漆膜的吸水率降低，电气强度增大，但树脂的水溶性变差，理想油度为37%；
With the increase of oil length, water absorption of the film reduces, while electrical strength increases, but water-dispersible was bad, the ideal oil length was 37%;
通过桐油与苯酚在酸性催化剂存在下反应，然后再在碱性催化剂存在与甲醛反应制得了一种热固性桐油改性酚醛树脂。
A new thermosetting modified phenolic resin by tung oil has been made through reaction between tung oil and phenol in condition of acid and then react to formaldehyde in condition of basicity.
本方法制成的亚麻油改性树脂的成本大大的降低，而用其制成的覆铜板性能不低于桐油改性树脂制成的覆铜板的性能。
The flaxseed oil modified resin has low cost and the copper-clad panel manufactured with it has performance not lower than that of copper-clad panel manufactured with tung oil modified resin.
通过桐油和本酚在催化剂存在下反应，然后再在碱性催化剂存在下与甲醛反应成功地制得了一种桐油改性甲阶酚醛树脂。
To obtain Successfully the PF resin, reaction of phenol with tung oil in the presence of catalyst was followed by the reaction with formaldehyde in the presence of alkaline catalyst.
结果表明，苯乙烯改性桐油基醇酸树脂涂膜具有快干、高硬度和耐水性好等优点。
The results showed that modified alkyd resin paints possess good properties such as fast drying, high hardness and excellent water resistance.
红外光谱表明了该双改性树脂的碳骨架上引入了桐油分子长碳链，具有一定的柔韧性和油溶性。
IR spectra showed that long chains of molecules of tung oil were bonded on the skeleton of boron phenolic resin.
红外光谱表明了该双改性树脂的碳骨架上引入了桐油分子长碳链，具有一定的柔韧性和油溶性。
IR spectra showed that long chains of molecules of tung oil were bonded on the skeleton of boron phenolic resin.