利用极化曲线测试法分析了不同碳材料和不同方法制备的铂碳复合电极的塔菲尔常数。
With the method of the polarization curves test, the Tafer constants of the platinum carbon composite electrodes made by different carbon materials and different preparation were tested.
采用极化曲线测试结合扫描电子显微镜分析技术，研究了退火对铝合金阳极的活性的影响。
The effects of annealing on the activity of al alloy anode were studied by measurement of polarization curves and analysis of SEM.
采用SEM观察了镁合金表面硅烷膜层形貌，并通过极化曲线测试评价了膜层耐腐蚀性能。
The morphological characterization and corrosion resistance of silane film were carried out via scanning electron microscope (SEM) and Tafel polarization curve, respectively.
研究改进了现行的钢铁件常温黑化工艺，通过极化曲线测试、耐蚀性测试、寿命测试得到了性能良好的常温亚硒酸体系黑化液。
A selenious acid type solution of better performance was obtained by the test of polarization curve, the test of corrosion resistance and the test of duration life.
通过静态腐蚀失重和动电位扫描极化曲线测试研究了所制备化合物的缓蚀性能，分析了缓蚀剂对碳钢的缓蚀机理，探讨了缓蚀剂分子与金属表面的作用方式。
The corrosion inhibiting mechanism of these compounds and mode of action between the corrosion inhibitors and metal surface were analysed and discussed. The results were as follows.
通过阳极极化曲线，测试涂层的耐蚀性能；
Thecorrosion resistance of the coatings were tested through anodic polarization curve. TheA.
测试比表面积、电阻率、孔径分布情况、空气电极的极化曲线、放电性能。
Specific surface area, resistivity, and distribution of pore diameter of air electrode were measured. Polarization curve and operating performance of air electrode have been tested.
采用动电位扫描法对成膜碳钢试样测试的阳极极化曲线显示，碳钢在腐蚀介质中处于钝化状态。
The anticathode of polarization curve of carbon steel with SAMs by changed - electrical voltage method suggested that carbon steel is passivation state in the rust medium.
通过电化学腐蚀测试测出阳极极化曲线，分析了在不同环境和溶液中的耐腐蚀性能。
Anode polarization curves were measured by electrochemistry corrosion and resisting causticity was analyzed in different condition and solution.
利用极化曲线技术、电化学阻抗测试技术等方法，研究了氯离子含量对黄壤土中碳钢腐蚀行为的影响。
The effects of chloride ion on corrosion of carbon steel in yellow soil were studied by using polarization curve technique, electrochemical impedance spectroscopy(EIS).
涂层的耐蚀性采用中性盐雾试验和5%盐水浸润试验，并测试涂层的阳极极化曲线综合进行比较。
The corrosion resistance of the coating was measured by neutral mist of salt experiment and soaking in 5%nacl solution. Moreover, the curves of positive polarization were give...
涂层的耐蚀性采用中性盐雾试验和5%盐水浸润试验，并测试涂层的阳极极化曲线综合进行比较。
The corrosion resistance of the coating was measured by neutral mist of salt experiment and soaking in 5%nacl solution. Moreover, the curves of positive polarization were give...