结果表明：随着变形温度的升高和应变速率的减小，位错密度减小，亚晶粒尺寸增大；
The results show that the dislocation density decreases and the subgrain sizes increase with the increase of deformation temperature and the decrease of the strain rate;
但是晶粒尺寸增大后晶界处因局部腐蚀电流密度增大将会在局部造成更深的腐蚀坑槽并降低耐候性；
The total quantity of corrosion surface defect is decreased due to the decrease of grain boundary energy with the increase of grain size and the atmospheric corrosion resistance is increased.
结果表明：随稀土含量的增加，合金的硬度和晶粒尺寸增大，加入适量的稀土，可提高合金的导电率。
The results show that hardness and grain size of the alloy increases as Rare Earth content is increasing.
XRD和TEM分析表明，随着溶剂介电常数和极性增加， 所生成产物的物相纯度、结晶度增高，晶粒尺寸增大。
XRD and TEM analyses show that the phase purity, crystallization and particle sizes of synthesized powders increase with the increase of the dielectric constant and polarity of the solvent.
随着沉积温度的降低，晶粒尺寸减小，晶格失配度增大；
With the increase of deposition temperatures, the crystalline sizes were increased but the crystal lattice distortions were decreased.
对于H68黄铜，随着晶粒尺寸的增大，出现锯齿屈服的临界应变量增大，锯齿波的最大应力振幅减小。
With the increase of the grain size of H68 brass, the critical plastic strain for the onset of serrations increases while the maximum stress amplitude of serrations decreases.
当磁场强度不变，随着磁场梯度的增大，初晶硅的偏聚量增加，晶粒尺寸变小。
The amount of segregated primary silicon grains increases with increasing magnetic gradient, whereas the grain size decreases.
随球磨时间的增加，样品的晶粒尺寸减小，晶格常数和晶格畸变增大。
With the grain size decreases, both the lattice constant and lattice distortion increase.
另外，随着热丝与衬底间距的增大，沉积出的多晶硅薄膜样品的晶化率明显减小，薄膜的晶粒尺寸也相应减小。
In addition, with the increasing distance between the filament and the substrate, the crystalline volume fraction and the grain size of poly-Si films notablely decrease.
动态再结晶行为随着应变速率的增大而逐渐被抑制，但晶粒尺寸反而减小；
The dynamic recrystallization behavior is inhibited with the increase of strain rate, but the grain size decreases.
应变速率减小，晶粒平均尺寸增大，晶粒变得圆整。
Average grain size increased and grain became round with strain rates reduction.
组织分离完成之后，晶粒的尺寸和形状系数随时间逐渐增大。
After the structure separation completed, the grain size and shape factor increased with the increase of the heating time.
随着变形温度的降低、变形程度和变形速率的增大，再结晶晶粒尺寸减小，再结晶体积分数增大。
With the decreases of deformation temperature and increases of deformation degree and deformation rate, the recrystallized grain size decreases and the recrystallization volume percent increases.
动态再结晶晶粒尺寸随着变形温度的升高而增大，随着应变速率的升高而减小。
The dynamically recrystallized grain size increases with increasing deformation temperature and reduces with increasing strain rate.
试验结果表明，试验钢在再加热过程中，奥氏体晶粒尺寸随加热温度的升高而增大；
The results showed that during reheating process, the austenite grain size in tested steel increased with an increase in the reheating temperature.
结果表明：球磨时间延长，振动频率提高和球料比的增大可有效地降低合金粉的晶粒尺寸。
The results show that the increase of the milling time, the vibration frequency and the charge ratio can effectively decrease the grain size of the alloy powder.
实验钢的硬度随平均晶粒尺寸的增大而逐渐降低，并呈近似的线性关系。
The hardness of the experimental steel decreases with the increase of average austenite grain size, which approximately keeps a linear relationship.
与奥氏体不锈钢、低碳钢等材料不同，随着TA 2合金试样晶粒尺寸的增大，纵波声速增大。
Different from the materials such as austenitic stainless steels, low carbon steels etc, the longitudinal velocity of TA2 alloy increased as the grain size increased.
催化剂上铁晶粒的尺寸随铁负载量的增加呈线性增大。
The size of iron crystallites on catalyst increased linearly with iron loading.
射线衍射（XRD）测试表明ITO薄膜的晶粒尺寸随膜内氧的摩尔分数增加而增大，随氧气比例增加薄膜（400）晶向消失。
XRD test showed that grain size of ITO films increased and crystallization direction(400) disappeared with more oxygen flow.
多晶体材料中晶粒尺寸的增大，对大多数材料来说，晶粒长大只在升高温度加热的时候发生。
The increase in average grain size of a polycrystalline material; for most materials, an elevated-temperature heat treatment is necessary.
动态再结晶晶粒尺寸随应变速率的增加而减小，随变形温度的增大而增大。
The size of dynamically recrystallized grain decreased with the increase of strain rate and increased with the increase of deformation temperature.
结果表明，随冷却速率的增大，先共析铁素体的晶粒尺寸减小，体积分数增大，针状铁素体增多；
The results show that with the increase of cooling rate, the grain size of proeutectoid ferrite decreases, the volume fraction of proeutectoid ferrite and acicular ferrite increases.
结合实验和模拟结果，得出该合金的晶粒尺寸、一次枝晶间距、二次枝晶臂间距随冷却速率增大而明显减小。
The results show that the grain average size and the primary and secondary dendrite arm space were obviously reduced with the increase of cooling rate.
当应变达到0.29时，平均晶粒尺寸缓慢地随应变增大而减小。
Nevertheless, after the strain reaches 0.29, the average grain size decreases slowly with the increase of strain.
当应变小于0.29时，平均晶粒尺寸明显地随应变增大而减小；
When the strain is below 0.29, the average grain size decreases obviously with the increase of strain.
随着晶粒尺寸的增大，薄膜矫顽力逐渐降低，过渡区噪声逐渐增大。
As the grain size increases, the coercivity gradually reduces and the transition noise increases.
随着晶粒尺寸的增大，薄膜矫顽力逐渐降低，过渡区噪声逐渐增大。
As the grain size increases, the coercivity gradually reduces and the transition noise increases.